光散射学报, 2003, 15 (3): 197, 网络出版: 2006-05-19   

纳米氧化锌的IR及其薄膜的UV光谱研究

Study on IR,UV-Vis Spectra of Nano- ZnO and Their Thin Films
作者单位
黑龙江大学化学化工学院,哈尔滨150080
摘要
采用溶胶-凝胶浸渍提拉法制备了纳米氧化锌薄膜.ZnO为六方晶系纤锌矿型,薄膜表面均匀致密,粒径尺寸约为10 nm,400℃焙烧后的粉体在451 cm-1处出现Zn-O伸缩振动,较体相材料向低波数移动了约29cm-1,膜中ZnO粒子的带边吸收位于363 nm,其吸光度值与膜层数间的较好线性关系说明可以将氧化锌溶胶中的纳米粒子较好地转移到基片上.
Abstract
The nanosized ZnO thin films were deposited by solgel technology. The ZnO particles crystallized in the wurtzite phase, which were welldistributed in the films with the mean particle size of about 10 nm. There was an absorption band at 451 cm-1 which was assigned to the ZnO stretching vibration in IR spectrum when the powders were roasted at 400℃. The band was redshifted about 29 cm-1 compared to ZnO bulk powder. The ZnO absorption onset of UVVis spectra was at about 363 nm. The linear relationship between the absorption intensity and the number of layers suggested that the nanoZnO were well transferred onto the quartz substrate.

程晓丽, 高山, 霍丽华, 赵经贵. 纳米氧化锌的IR及其薄膜的UV光谱研究[J]. 光散射学报, 2003, 15(3): 197. 程晓丽, 高山, 霍丽华, 赵经贵. Study on IR,UV-Vis Spectra of Nano- ZnO and Their Thin Films[J]. The Journal of Light Scattering, 2003, 15(3): 197.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!