中国激光, 2004, 31 (3): 339, 网络出版: 2006-06-12   

晶体光谱特性 下载: 600次

Spectral Properties of Nd3+:Y0.5Gd0.5VO4 Crystal
作者单位
1 中国科学院安徽光学精密机械研究所,安徽 合肥 230031
2 中国科学院上海光学精密机械研究所,上海 201800
3 昆山上光富晶光电材料有限公司,江苏 昆山 215316
摘要
测量了0.8 at.-% Nd3+:Y0.5Gd0.5VO4的吸收光谱和荧光发射谱,光谱显示该晶体在808.5 nm有很强的偏振光吸收峰,且π偏振光(E∥C)吸收远强于σ偏振光(E⊥C)吸收,半高宽度分别为4.5 nm和12 nm,吸收截面分别为19.69×10-20 cm2和6.41×10-20 cm2;其荧光发射( 4F3/2→ 4I11/2跃迁)峰值波长在1064 nm,半高宽度为3.7 nm; 4F3/2→ 4I11/2跃迁的荧光寿命为110 μs;光谱特性表明Nd3+:Y0.5Gd0.5VO4晶体是潜在的高效率激光晶体材料.
Abstract
In this paper, the absorption spectrum and the fluorescence (or emission) spectrum of the Nd 3+∶ Y 0.5Gd 0.5VO 4 crystal were measured; Its strong absorption wavelength is at 808 5 nm; Its π polarized absorption is stronger than its σ polarized absorption and their FWHM are 4 5 nm and 8 5 nm, respectively, their absorption cross section are 19 69×10 -20 cm 2 and 6 41×10 -20 cm 2, respectively; Fluorescence (or emission) spectrum FWHM at 1064 nm is 3 7 nm; Its fluorescence lifetime is 110 μs (Nd:0.8at.-%); These properties show that Nd3+:Y0.5Gd0.5VO4 crystal is a kind of potential efficient laser material.

张连翰, 杭寅, 孙敦陆, 钱小波, 李世锋, 殷绍唐. 晶体光谱特性[J]. 中国激光, 2004, 31(3): 339. 张连翰, 杭寅, 孙敦陆, 钱小波, 李世锋, 殷绍唐. Spectral Properties of Nd3+:Y0.5Gd0.5VO4 Crystal[J]. Chinese Journal of Lasers, 2004, 31(3): 339.

本文已被 7 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!