中国激光, 2004, 31 (4): 457, 网络出版: 2006-06-12   

光致变色俘精酸酐用于可擦写全息图像存储的研究

Study of Holographic Image Storage in Rewritable Photochromic Fulgide Material
作者单位
1 中国科学院西安光学精密机械研究所瞬态光学技术国家重点实验室, 陕西 西安 710068
2 中国科学院物理化学技术研究所,北京 100101
摘要
对一种新型可擦重写有机光致变色材料――俘精酸酐/聚甲基丙烯酸甲脂(PMMA)薄膜的光致变色双稳态吸收光谱进行了测量,呈色态的吸收峰在513 nm,无色态的吸收峰在370 nm。利用该双稳态特性,在10 μm俘精酸酐/PMMA薄膜上进行全息图像光存储。实验用氩离子激光器514.5 nm波长作为记录光源,测量了衍射效率与曝光量的关系,最大衍射效率约为1%,最佳曝光量约1 J/cm2。获得了存储于样品上的全息干涉条纹和参考光再现的衍射像,分析了影响衍射图像像质的因素。记录在样品上的全息图在室温下黑暗处可以保存一年以上,用紫外光可以擦除记录的全息图,进行多次记录、读出和擦除操作。结果表明,俘精酸酐可以作为一种性能优良的可擦写全息光存储材料。
Abstract
A new type of organic photochromic material―fulgide/PMMA film was investigated as a rewritable holographic recording medium. The bistable absorption spectra of the fulgide/PMMA film were measured. The maximum absorption of the colored state was centered at 513 nm, the peak absorption of the bleached state was at 370 nm. Based on the bistable states of the photochromic fulgide, holographic images were stored on the 10 μm film. Argon laser (514.5 nm) was used as recording light. The relation between the diffraction efficiency and the exposure was measured, which showed that the maximal diffraction efficiency was about 1% under the exposure 1 J/cm2 or so. Holographic gratings recorded on the film and diffraction images recovered by the reference beam were obtained. Factors influencing the recovery image′s quality were analyzed. The holographic gratings recorded on the film can be kept for over one year in darkness at room temperature, which can be erased by UV light. The sample can be written, read and erased in many times. The experimental results show that the fulgide can be used as a good rewritable holographic storage material.

王英利, 姚保利, 郑媛, 门克内木乐, 雷铭, 陈国夫, 陈懿, 樊美公, 闫起强, 韩勇, 孟宪娟. 光致变色俘精酸酐用于可擦写全息图像存储的研究[J]. 中国激光, 2004, 31(4): 457. 王英利, 姚保利, 郑媛, 门克内木乐, 雷铭, 陈国夫, 陈懿, 樊美公, 闫起强, 韩勇, 孟宪娟. Study of Holographic Image Storage in Rewritable Photochromic Fulgide Material[J]. Chinese Journal of Lasers, 2004, 31(4): 457.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!