高掺镁铌酸锂晶体周期极化及倍频特性研究

STUDY ON PERIODICALLY POLED CHARACTERISTICS OF MgO:LiNbO3 AND SECOND HARMONIC GREEN LIGHT GENERATION
作者单位
1 南开大学,物理科学学院光子学中心,天津,300071
2 南开大学,泰达应用物理学院,天津,300457
摘要
研究了掺镁(5mol%)铌酸锂晶体的周期极化特性,发现晶体的极化矫顽场仅为3kV/mm,根据镁掺杂对晶体本征缺陷的影响解释了极化矫顽场降低的原因.采用短脉冲极化电场,对极化电流的热效应进行抑制从而消除了晶体均匀性对制备周期极化光栅的影响,在1mm厚的掺镁(5mol%)铌酸锂晶体上成功制备出了均匀的周期极化光栅.在室温下,利用1.064μm的Nd:YAG调Q激光器对得到的周期极化掺镁铌酸锂晶体进行了倍频实验,在输入功率为75mW时,得到3.5mW的532nm倍频绿光输出,转换效率为4.6%.
Abstract
The periodically poled characteristics of LiNbO3 doped 5mol% MgO were investigated and the domain reversal field was found to be 3kV/mm. According to the influence of MgO doped on the crystal defect, the decrease reason of the domain reversal field was explained. By using short-pulse field, the periodically poled grating was successfully fabricated in 1.0mm thick MgO:LiNbO3. Second harmonic green light generation in periodically poled MgO:LiNbO3 was demonstrated. The green light power of 3.5mW at 532nm is obtained when the fundamental power is 75mW, and the conversion efficiency is 4.6%.

颜博霞, 姚江宏, 陈亚辉, 许京军, 张光寅. 高掺镁铌酸锂晶体周期极化及倍频特性研究[J]. 红外与毫米波学报, 2005, 24(3): 213. 颜博霞, 姚江宏, 陈亚辉, 许京军, 张光寅. STUDY ON PERIODICALLY POLED CHARACTERISTICS OF MgO:LiNbO3 AND SECOND HARMONIC GREEN LIGHT GENERATION[J]. Journal of Infrared and Millimeter Waves, 2005, 24(3): 213.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!