光学学报, 2006, 26 (5): 783, 网络出版: 2006-06-01   

Au/SiO2纳米复合型材料的光吸收性质

Optical Absorption Properties of Au-SiO2 Nanocomposites
作者单位
1 宁波大学理学院物理系, 宁波 315211
2 新加坡南洋理工大学电子工程学院, 新加坡 639798
摘要
在室温下用离子束溅射沉积工艺在石英基材上生成Au-SiO2复合薄膜。把生成薄膜从500~900 ℃(分别保温5 min)分五个不同温度进行退火处理。用X光衍射方法(XRD)对薄膜结构进行了测试,得到Au-SiO2纳米复合薄膜未退火(as-dep)和退火后的X射线衍射谱;透射电子显微镜(TEM)观察了经过700 ℃退火处理复合薄膜中Au粒子在薄膜中分布状态和颗粒大小。用分光计测试薄膜光吸收特性,吸收光谱范围为190~1000 nm,发现退火温度从500~700 ℃,光谱吸收峰有明显红移存在,而在更高温度吸收峰的位置和强度几乎都不变。这与X射线衍射检测吻合。并用德鲁特(Drude)模型给于理论解释。
Abstract
Ion beam co-sputtering technique is used to deposit Au-SiO2 nanocomposite films on quartz at room temperature. The nanocomposite films are annealed at different temperatures from 500~900 ℃ for 5 minutes. The film phases are identified by X-ray diffraction (XRD),the XRD spectra of Au-SiO2 nanocomposite as-deposited and annealed are obtained. Transmission electronic microscopy (TEM) is used to check Au particles distribution and size in the film annealed at 700 ℃. Optical absorption spectra are recorded in 190~1000 nm with a spectrometer. The absorption peak has a clear red-shift with increasing temperature in 500~700 ℃, and both position and intensity of the peak seem not to alter at higher temperature. It agrees well with the detection in XRD. With Drude model the absorption peak is explained theoretically.

王勤诚, 俞国庆. Au/SiO2纳米复合型材料的光吸收性质[J]. 光学学报, 2006, 26(5): 783. 王勤诚, 俞国庆. Optical Absorption Properties of Au-SiO2 Nanocomposites[J]. Acta Optica Sinica, 2006, 26(5): 783.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!