中国激光, 2006, 33 (5): 687, 网络出版: 2006-06-01   

GeS2-Ga2S3-CdS硫系玻璃的电致二阶非线性光学效应

Second-Order Optical Nonlinearity of Electrical Poling in GeS2-Ga2S3-CdS Chalcogenide Glass
作者单位
1 武汉理工大学硅酸盐材料工程教育部重点实验室,湖北 武汉 430070
2 武汉理工大学材料科学与工程学院, 湖北 武汉 430070
摘要
采用熔融-急冷法制备了在可见光区有较高透射率的GeS2-Ga2S3-CdS硫系玻璃,通过麦克尔(Maker)条纹法观察电场-温度场极化的片状样品中的二阶非线性光学效应,并讨论了该效应的机理。结果表明,在270 ℃极化30 min,当极化电压大于2 kV/mm时,观察到明显的二阶非线性光学效应,且二次谐波强度的大小随极化电压的增大而增大。二次谐波效应的产生是玻璃中的偶极子在电场作用下的取向调整,破坏了玻璃的宏观各向同性所致,二次谐波强度出现最大值的入射角与偶极子的取向调整程度有关。
Abstract
Chalcogenide glasses of GeS2-Ga2S3-CdS system with high transmittance in visible region were obtained by melt-quenching method. A prominent second harmonic generation (SHG) was observed from thermally electrical poled chalcogenide glass by Maker-fringe method and its mechanism was discussed. After thermal poling treatment at 270 ℃ for 30 min, SHG was seen from glasses poled voltage above 2 kV/mm, and the second harmonic intensity increased as the poling voltage increased. The origin of the SHG induced in the glass is associated with the reorientation of diploes under direct current (DC) and therefore breaking the inversion symmetry of the glass. The angle of incidence that maximum second harmonic intensity was generated is relative to the degree of dipoles reorientation.

顾少轩, 胡海平, 郭海涛, 袁凯, 赵修建. GeS2-Ga2S3-CdS硫系玻璃的电致二阶非线性光学效应[J]. 中国激光, 2006, 33(5): 687. 顾少轩, 胡海平, 郭海涛, 袁凯, 赵修建. Second-Order Optical Nonlinearity of Electrical Poling in GeS2-Ga2S3-CdS Chalcogenide Glass[J]. Chinese Journal of Lasers, 2006, 33(5): 687.

本文已被 4 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!