应用光学, 2014, 35 (4): 670, 网络出版: 2014-09-15   

多结电池宽光谱ZnS/Al2O3/MgF2减反射膜的设计与分析

ZnS/Al2O3/MgF2 antireflection coating with wide spectrum for GaAs multi-junction solar cells
作者单位
云南师范大学 太阳能研究所,教育部可再生能源材料先进技术与制备重点实验室,云南省农村能源工程重点实验室, 云南 昆明 650092
摘要
为了提高砷化镓(GaAs)多结太阳电池的光电转换效率, 设计了宽光谱(300 nm~1 800 nm)ZnS/Al2O3/MgF2三层减反射膜, 分析了各层的厚度及折射率对三层膜系有效反射率的影响。结果表明: 对于整个波长, ZnS厚度对有效反射率的影响要大于Al2O3和MgF2, MgF2厚度对有效反射率的影响最小; 适当减小MgF2的折射率或增加ZnS的折射率可得到更低的有效反射率。同时, 当 ZnS, Al2O3和MgF2的最优物理厚度分别为52.77 nm, 82.61 nm, 125.17 nm时, 此时最小有效反射率为2.31%。
Abstract
ZnS/Al2O3/MgF2 three-layer antireflection coating with wide spectrum (300 nm~1800 nm) was designed in order to improve the photoelectric conversion efficiency of GaAs multi-junction solar cells. The influence of each layers thickness and refractive index on the effective reflectance of film system was analyzed. The results show that the impact of the film thickness of ZnS is greater than that of Al2O3 and MgF2 on the effective reflectance in the whole wavelength,and the impact of MgF2 is the lowest; decreasing the refractivity of MgF2 or increasing the refractivity of ZnS proportionally can get lower effective reflectance. Furthermore, when the optimal physical thickness of ZnS,Al2O3 and MgF2 is 52.77 nm, 82.61 nm and 125.17 nm respectively by programming calculation,the minimum effective reflectance is 2.31%.

肖祥江, 涂洁磊, 白红艳. 多结电池宽光谱ZnS/Al2O3/MgF2减反射膜的设计与分析[J]. 应用光学, 2014, 35(4): 670. Xiao Xiangjiang, Tu Jielei, Bai Hongyan. ZnS/Al2O3/MgF2 antireflection coating with wide spectrum for GaAs multi-junction solar cells[J]. Journal of Applied Optics, 2014, 35(4): 670.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!