DLC/Ag/DLC复合多层薄膜光学性能

Studay on Optical Property of DLC/Ag/DLC Multilayer Films
作者单位
1 上海摩根碳制品有限公司, 上海 200241
2 中南大学 物理科学与技术学院, 湖南 长沙 410083
摘要
采用等离子体增强化学气相沉积类金刚石(DLC)薄膜、高真空磁控溅射镀膜设备溅射Ag靶的方法制备了不同厚度Ag、DLC层的DLC/Ag/DLC多层膜,分别用紫外可见分光光度计、四探针测试仪对样品的光学性能、电学性能进行了测试。结果表明,随着Ag层厚度的增加,DLC/Ag/DLC多层膜透射率先增后减,外层DLC薄膜和内层DLC薄膜对透射率影响基本一致,随着厚度增加透射率先增后减,在内外层厚度为40 nm,Ag夹层厚度为16 nm时,DLC(30 nm)/Ag(16 nm)/DLC(40 nm)膜在550 nm处的透射率高达94.4%,电气指数高达112.4×10-3 Ω-1,远远超过现有透明导电膜的电气指数(FTC≈20×10-3 Ω-1)。
Abstract
DLC/Ag/DLC multilayer films with different Ag and DLC thickness were prepared with high-vacuum magnetron sputtering. DLC layers were prepared by plasma enhanced chemical vaporation deposition method. The optical and electrical properties of samples were studied with a UV-vis pectrophotometer and a four-point probe,respectively. The results indicate that with the increase of the thickness of the Ag layer, the transmittance firstly increases and then decreases. With the increase of the thickness of the inner or outer DLC layer, the transmittance also firstly increases and then decreases. With the thickness of multilayer films up to DLC(30 nm)/Ag(16 nm)/DLC(40 nm), the film has a high optical transmittance of 94.4% at 550 nm and the electrical index is up to 112.4×10-3 Ω-1 which is much higher than that of the existing transparent optical conducting films (FTC≈20×10-3 Ω-1).

张德恒, 徐照方, 李伯勋. DLC/Ag/DLC复合多层薄膜光学性能[J]. 光学学报, 2008, 28(10): 2031. Zhang Deheng, Xu Zhaofang, Li Boxun. Studay on Optical Property of DLC/Ag/DLC Multilayer Films[J]. Acta Optica Sinica, 2008, 28(10): 2031.

本文已被 6 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!