光学学报, 2014, 34 (9): 0916001, 网络出版: 2014-08-15
新型黄绿色荧光粉BaMoO4:Pr3+的制备与光致发光性质研究
Preparation and Photoluminescent Properties of a Novel Yellow-Green BaMoO4:Pr3+ Phosphor
材料 高温固相法 光致发光 materials high-temperature solid-phase method photoluminescence BaMoO4:Pr3+ BaMoO4:Pr3+
摘要
采用高温固相法成功合成了新型BaMoO4:Pr3+黄绿色荧光材料,并对其晶体结构、形貌和发光性质进行了研究。X射线衍射(XRD)测试结果表明在1300 ℃制备的样品具有白钨矿类结构晶体,样品的形貌在扫描电镜(SEM)显示下呈不规则外形。荧光样品激发光谱由强的电荷迁移跃迁(CT)带和Pr3+离子的特征激发峰组成,主激发峰位于447 nm(3H4→3P2)、472 nm(3H4→3P1)和485 nm(3H4→3P0);其发射谱峰分别位于527 nm(3P1→3H4,5)、542 nm和551 nm (3P0→3H5)、596 nm(1D2→3H4)、614 nm(3P0→3H6)和642 nm(3P0→3F2),最强发射峰位于642 nm处。获得Pr3+的最佳掺杂摩尔分数为0.2%~0.3%。研究表明: BaMoO4:Pr3+是一种有望应用于蓝光发光二极管(LED)有效激发的黄绿色荧光粉材料。
Abstract
A novel yellow-green BaMoO4:Pr3+ phosphor is successfully prepared via high-temperature solid-phase method, and its structure, morphology and luminescence properties are studied. The X-ray diffraction (XRD) patterns results show that the samples obtained after sintered at 1300 ℃ have the scheelite structure. The morphology of the sample has irregular shapes which can be observed by scanning electronic microscopy (SEM). The excitation spectrum of phosphor sample consists of strong charge transfer (CT) band and characteristic excitation peaks of Pr3+. The main excitation peaks are at 447 nm (3H4→3P2), 472 nm(3H4→3P1) and 485 nm(3H4→3P0), respectively. The emission spectrum peaks locate at 527 nm(3P1→3H4,5), 542 nm and 551 nm (3P0→3H5), 596 nm(1D2→3H4), 614 nm(3P0→3H6) and 642 nm(3P0→3F2), respectively. The strongest peak appears at 642 nm. The optimum doping mole fraction of Pr3+ is 0.2%~0.3%. The results show that BaMoO4:Pr3+ is a promising yellow-green phosphor which can be effectively excited by blue light emitting diode (LED).
张伟杰, 冯文林, 程雪羚, 熊博文, 吕立康. 新型黄绿色荧光粉BaMoO4:Pr3+的制备与光致发光性质研究[J]. 光学学报, 2014, 34(9): 0916001. Zhang Weijie, Feng Wenlin, Cheng Xueling, Xiong Bowen, Lü Likang. Preparation and Photoluminescent Properties of a Novel Yellow-Green BaMoO4:Pr3+ Phosphor[J]. Acta Optica Sinica, 2014, 34(9): 0916001.