微腔有机电致发光器件的角度依赖性

Angle Dependence of Microcavity Organic Light-emitting Device
作者单位
1 吉林建筑工程学院 材料科学与工程学院, 吉林 长春 130021
2 吉林大学 物理学院, 吉林 长春130021
3 中国科学院 长春光学精密机械与物理研究所, 吉林 长春130033
摘要
设计并制作了两个器件,一个是微腔有机电致发光器件(MOLED):G/DBR/ITO/NPB(46 nm)/DPVBi(20 nm)/Alq3(56 nm)/LiF(1 nm)/Al(150 nm);一个是无腔器件(OLED):G/ITO/NPB(46 nm)/DPVBi(20 nm)/Alq3(56 nm)/LiF(1 nm)/Al(150 nm)。测试并分析了器件性能。OLED在电流密度30 mA/cm2时的电致发光(EL)光谱随观测角度由0°~70°都是一宽谱带,是发光层DPVBi的特征发光谱,峰值都在452 nm处,半峰全宽均为70 nm,色坐标均为(x=0.18,y=0.19),无腔器件没有角度依赖性。相同电流密度下,微腔器件的EL谱随观测角度由0°~70°,发光峰值蓝移,由472 nm逐渐移至428 nm;峰值相对强度渐弱,由0.32变至0.02;半峰全宽由14 nm增加至120 nm;色坐标由(x=0.14,y=0.10)变至(x=0.19,y=0.25),颜色由紫蓝变成蓝白到接近白色。微腔器件具有明显的角度依赖性。
Abstract
We designed and made two devices, one is microcavity organic light-emitting device (MOLED), and the other is non-microcavity device (OLED). The structures of MOLED is G/DBR/ITO/NPB (46 nm)/DPVBi (20 nm)/Alq3 (56 nm)/LiF (1 nm)/Al (150 nm); OLED is G/ITO/NPB (46 nm)/DPVBi(20 nm)/Alq3 (56 nm)/LiF (1nm)/Al (150 nm). The performances of MOLED and OLED were tested and analyzed. The OLEDs electroluminescent (EL)-angle curve, at 30 mA/cm2 and changing the angle from 0° to 70°, is a broad spectrum. It is the characteristic spectrum of DPVBi luminescence layer, which peaked at 452 nm, the full width at half maximum (FWHM) is 70 nm. The color coordinates (CIE) are (x=0.18, y=0.19). It was proved that OLED has no angle dependence.The MOLED EL-angle curve at the same current of 30 mA/cm2 is a narrow spectrum. We can see that, along with the detecting angle changing from 0° to 70°, the EL peak values decreases from 472 nm to 428 nm, namely blue shift. The peak intensity also decreased. The FWHM became larger from 14 nm to 120 nm. The CIE coordinates change from (x=0.14, y=0.10) to (y=0.19, 0.25), the color changes into blue-white from purple-orchid. All of the above proved that the MOLED obviously has angle dependence. The angle dependence of MOLED is disadvantage for flat display application, thus we need reduce it. But this characteristics is virtue and necessary for organic microcavity laser.

张春玉, 陆景彬, 孙成林, 秦莉, 肖力光, 任慧, 王成. 微腔有机电致发光器件的角度依赖性[J]. 发光学报, 2009, 30(6): 734. ZHANG Chun-yu, LU Jing-bin, SUN Cheng-lin, QIN Li, XIAO Li-guang, REN Hui, WANG Cheng. Angle Dependence of Microcavity Organic Light-emitting Device[J]. Chinese Journal of Luminescence, 2009, 30(6): 734.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!