ZL114A铝合金激光填丝焊接工艺及显微组织研究

Research on Microstructure and Processing Parameters of Filler Rod Laser Welding Joint of ZL114A Al Alloy
作者单位
华中科技大学 材料科学与工程学院,武汉 湖北 430074
摘要
对ZL114A铝合金进行了YAG激光填丝焊接实验,研究了激光焊接工艺参数与焊缝成形质量的关系,并利用光学显微镜、扫描电镜(SEM)、能谱(EDS)等实验方法分析了ZL114A激光填丝焊接接头的显微组织,讨论了焊接熔池的冶金产物。结果表明:ZL114A铝合金激光填丝焊的功率密度阈值比非填丝激光焊略高,当激光的功率密度超过阈值时可以获得成形稳定的焊缝;焊缝主要组成相为α(Al)、共晶Si和Mg2Si。
Abstract
Laser welding was carried out on the ZL114A Al alloy sheet with filler rod,the relationship between the laser welding processing parameters and weld forming quality was explicated,and the microstructure of the welding seams were analyzed with optical microscope,SEM,and EDS. The metallurgical products in the welding pool were analyzed. The results show that the power density threshold of the Laser welding ZL114A with filler rod is slightly higher than the non-filling laser welding,when the laser power density exceeds the threshold a stable forming weld seam is available. The main phases of the weld seam are α (Al),eutectic Si and Mg2Si.

汪永阳, 黄安国, 李颉, 李昊, 刘建华, 胡伦骥. ZL114A铝合金激光填丝焊接工艺及显微组织研究[J]. 应用激光, 2009, 29(5): 393. Wang Yongyang, Huang Anguo, Li Jie, Li Hao, Liu Jianhua, Hu Lunji. Research on Microstructure and Processing Parameters of Filler Rod Laser Welding Joint of ZL114A Al Alloy[J]. APPLIED LASER, 2009, 29(5): 393.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!