YAG-MIG复合焊接ZL-114A铝合金的接头组织与性能研究

Microstructure and properties of YAG-MIG hybrid welding joint of ZL-114A aluminum alloy
作者单位
1 华中科技大学 材料科学与工程学院,武汉 430074
2 北京航星机器制造公司,北京 100013
摘要
为了研究ZL-114A铝合金YAG激光-熔化极惰性气体保护(MIG)电弧复合焊接接头性能,采用拉伸试验和扫描电子显微镜对其力学性能和显微组织进行了测试分析。由于焊接固有的快速冷却特性及进口4047焊丝中细化晶粒元素(Ti)的存在,焊缝金属组织普遍较铸造组织细小,而且与采用的焊接线能量有关;靠近熔合线附近的晶粒粗化及固溶相的析出导致其硬度陡降,成为所谓的“软化区”,是接头最脆弱部分,但其宽度及粗化程度较一般MIG电弧焊小,接头拉伸强度为母材的80%左右,断口呈脆性断裂特征。实验结果表明,采用适当的工艺参量,YAG-MIG复合焊接可以在较高的速率下得到高质量的焊接接头,是一种理想的铝合金高效焊接技术。
Abstract
In order to study the performance of YAG-MIG(metallic inert gas)arc hybrid welding joint of ZL-114A aluminum alloy,the tensile test and scanning electronic microscope were adopted to analyze the mechanical properties and microstructure of welded joint. The microstructure of the bead was smaller than that of base metal because of the inherent splat cooling of welding and the beneficial effect of titanium(Ti),and the microstructure was smaller when the heat input was smaller. The crystal of heat affected zone(HAZ)was coursing,and had a softened zone near the bond line because of the precipitation and dissolution of the solid solution phase in base metal. The softened zone was the worst mechanics in the joint,which in the YAG-MIG hybrid welding was usually much narrower than that in the single MIG welding. The tensile-strength of the YAG-MIG hybrid welding joint was up to 80% of the base metal,the fracture characteristic belonged to brittle fracture. The results show that the high quality joint can be achieved in a high welding speed when the welding parameter is appropriate,so the YAG-MIG hybrid welding is an ideal welding technique for aluminum alloy with high efficiency.

余阳春, 王春明, 邓玉平, 余圣甫, 刘刚, 王志敏, 顾兰. YAG-MIG复合焊接ZL-114A铝合金的接头组织与性能研究[J]. 激光技术, 2008, 32(6): 0601. YU Yang-chun, WANG Chun-ming, DENG Yu-ping, YU Sheng-fu, LIU Gang, WANG Zhi-min, GU Lan. Microstructure and properties of YAG-MIG hybrid welding joint of ZL-114A aluminum alloy[J]. Laser Technology, 2008, 32(6): 0601.

本文已被 5 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!