发光学报, 2010, 31 (6): 796, 网络出版: 2011-02-15
Durability and Near-infrared Photoluminescence of Er3+-doped (ZnO)1-x-y(P2O5)x(B2O3)y Glass Systems
Durability and Near-infrared Photoluminescence of Er3+-doped (ZnO)1-x-y(P2O5)x(B2O3)y Glass Systems
摘要
Er3+掺杂的(ZnO)1-x-y(P2O5)x(B2O3)y玻璃具有优良的光学性质。沸水煮沸实验结果表明, 该类玻璃具有较高的环境稳定性。与(Er2O3)z(ZnO)1-x-z(P2O5)x-z 类玻璃相比, Er3+掺杂的该类玻璃在1.5 μm峰值位置的光谱半峰全宽超过110 nm, 而且具有较高的猝灭浓度。
Abstract
Er3+-doped (B2O3)y(ZnO)1-x-y(P2O5)x glass with excellent optical properties was prepared. The glass was proved to have the high stability by the investigation of the durability in boiling water. The spectral characters of the glass at about 1.5 μm changed a lot with the doped contents of both Er3+ and B2O3. Comparing with Er3+-doped zinc phosphate glass systems, the glass prepared in our laboratory exhibits a larger quenching concentration and a much broader emission band at 1.54 μm.
王阳, 张继森, 吕少哲, 孙秀平, 夏楠. Durability and Near-infrared Photoluminescence of Er3+-doped (ZnO)1-x-y(P2O5)x(B2O3)y Glass Systems[J]. 发光学报, 2010, 31(6): 796. WANG Yang, ZHANG Ji-sen, LU Shao-zhe, SUN Xiu-ping, XIA Nan. Durability and Near-infrared Photoluminescence of Er3+-doped (ZnO)1-x-y(P2O5)x(B2O3)y Glass Systems[J]. Chinese Journal of Luminescence, 2010, 31(6): 796.