三基色量子点的制备与白光的实现

PREPARATION OF TRICHROMATIC QUANTUM DOTS: SOURCE OF WHITE LIGHT
作者单位
中国科学院上海技术物理研究所 红外物理国家重点实验室, 上海200083
摘要
采用化学溶液方法, 以乙基黄原酸盐作为壳层前驱体, 制备了红绿蓝三色发光的CdSe/ZnS核壳量子点.以乙基黄原酸锌为前驱体形成ZnS壳层包覆CdSe核量子点, 通过调节反应温度与反应气氛等条件获得了发绿光(542nm)及蓝光(483nm)的核壳量子点.以乙基黄原酸镉和乙基黄原酸锌分别作为壳层CdS及ZnS的前驱体制备了发红光(612nm)CdSe/CdS/ZnS核/多壳结构量子点.紫外-可见吸收光谱、荧光光谱及透射电镜研究结果表明, 通过条件调节, 温度较低时(约230℃)注入乙基黄原酸锌后量子点发光峰出现红移, 而温度较高时(约260℃)则发生蓝移.通过不同发光颜色的量子点的混合实现了三基色白光.
Abstract
Based on chemical solution-process method, red, green, and blue-luminescent CdSe/ZnS semiconductor core/shell quantum dots were successfully prepared by utilizing ethylxanthates as precursors of shell layers. Green-luminescent (542nm) and blue-luminescent (483nm) core/shell quantum dots were synthesized by capping the CdSe core quantum dots with ZnS shell layers from zinc ethylxanthate precursors and manipulating reaction temperature with the presence of oxygen. The red color (612nm) CdSe/CdS/ZnS core/multishelled quantum dots were prepared by capping of CdS and ZnS shell layers from cadmium ethylxanthate and zinc ethylxanthate precursors. Results from UV-vis absorption spectra, photoluminescence spectra and transmission electron microscopy (TEM) indicated that the emission red-shifted if the ZnS capping of CdSe dots is processed at a lower temperature (about 230 ℃ ), while blue-shifted at a higher temperature (about 260 ℃ ). Trichromatic white light was obtained via mixing of red, green, and blue-luminescent quantum dots.

乐阳, 葛美英, 孙艳, 陈鑫, 戴宁. 三基色量子点的制备与白光的实现[J]. 红外与毫米波学报, 2010, 29(6): 427. YUE Yang, GE Mei-Ying, SUN Yan, CHEN Xin, DAI Ning. PREPARATION OF TRICHROMATIC QUANTUM DOTS: SOURCE OF WHITE LIGHT[J]. Journal of Infrared and Millimeter Waves, 2010, 29(6): 427.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!