激光技术, 2011, 35 (2): 285, 网络出版: 2011-03-10   

表面污染物诱导熔石英损伤的热力学数值模拟

Thermal stress simulation of laser induced damage of fused silica by contamination on the surface
作者单位
中国工程物理研究院 激光聚变研究中心, 绵阳 621900
摘要
为了研究高功率固体激光装置内污染诱导光学元件损伤问题, 基于有限元数值方法, 结合污染物诱导熔石英损伤机理, 给出了熔石英样片在高功率脉冲激光辐照下的温度场和应力场分布。结果表明, 激光脉冲辐照过程中主要以污染物的温度升高为主, 最高至2800K, 而样片温升不大, 仅为7K; 在激光脉冲辐照后100μs的时间内, 样片表面中心快速升温至2200K, 而边缘处仅为700K, 在较短的距离内温度变化剧烈, 由此产生的热应力导致表面发生损伤; 损伤区域中心表现为压应力, 边缘为拉应力, 最大可达30-73MPa。测试了污染物诱导样片损伤斑的微观显微形貌, 实验结果和理论计算结果符合较好。
Abstract
In order to study the laser-induced damage mechanism in inertial confinement fusion system, temperature and thermal stress distributions in the fused silica, heated by repetition frequency laser, were given by means of finite element methods. The simulated results indicate the temperature of the contaminations rise to 2800K during the pulse laser irradiation, but the fused silica’s temperature mainly rise from 300K to 2200K in 100μs after irradiation, and damage induced by the thermal stress occurs. The strong compressive in the damage region is about 30-73MPa. The highest stress outside the damage region is deviatoric hoop stress. The damage morphologies were tested by means of optical microscopy. The simulated outcomes correspond to the experiment result.

苗心向, 袁晓东, 程晓锋, 贺少勃, 郑万国. 表面污染物诱导熔石英损伤的热力学数值模拟[J]. 激光技术, 2011, 35(2): 285. MIAO Xin-xiang, YUAN Xiao-dong, CHENG Xiao-feng, HE Shao-bo, ZHENG Wan-guo. Thermal stress simulation of laser induced damage of fused silica by contamination on the surface[J]. Laser Technology, 2011, 35(2): 285.

本文已被 5 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!