Ag纳米颗粒有机薄膜受激辐射增强研究

Silvernanoparticleenhanced stimulated emission of organic thin films
作者单位
1 西安交通大学 电子与信息工程学院 陕西省信息光子技术重点实验室电子物理与器件教育部重点实验室,陕西 西安710049
2 西安洪庆高技术研究所 物理室,陕西 西安710025
摘要
为进一步降低有机半导体材料的激射阈值,文章研究利用银纳米颗粒的表面等离子体共振效应来实现对有机半导体薄膜受激辐射的增强.将制备好的Ag纳米溶液旋涂于玻璃基底上,然后在其上再旋涂PS:Alq3:DCJTB有机薄膜发光层,构成平面波导结构.用355nm波长的YAG激光泵浦样品。实验发现:相比于无Ag纳米颗粒情况,有Ag纳米颗粒时端面受激发射最大增强10.38倍,激射阈值从2.0mJ/cm2左右降低到0.5mJ/cm2左右;垂直表面受激发射最大增强6.13倍,激射阈值从2.5mJ/cm2左右降低到1.5mJ/cm2左右.该研究对实现低阈值有机半导体激光器具有重要意义.
Abstract
To further reduce the lasing threshold of organic semiconductor materials, the surface plasmon resonance effect of silver nanoparticles was investigated. The prepared silver nanoparticle solution was spincoated on glass substrate, and then PS:Alq3:DCJTB organic thin film was spincoated on the surface of Ag nanoparticles, and thus formed a planar waveguide. Pumped by YAG (λ=355nm) laser, the stimulated emission results show that compared with the case without Ag nanoparticles, the Agnanoparticleenhanced edge stimulated emission increases 10.38fold and its lasing threshold reduces to 0.5 mJ/cm2 from 2.0 mJ/cm2. The vertical surface stimulated emission increases 6.13fold and its lasing threshold reduces to about 1.5 mJ/cm2 from 2.5 mJ/cm2. This work may be of great significance in the realization of lowthreshold organic semiconductor lasers.

赵选科, 吴朝新, 徐国金, 梁世雄, 侯洵. Ag纳米颗粒有机薄膜受激辐射增强研究[J]. 红外与毫米波学报, 2011, 30(3): 217. ZHAO XuanKe, WU ZhaoXin, XU GuoJin, LIANG ShiXiong, HOU Xun. Silvernanoparticleenhanced stimulated emission of organic thin films[J]. Journal of Infrared and Millimeter Waves, 2011, 30(3): 217.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!