多层氧化物复合阴极透明OLED器件

Transparent Organic Light Emitting Diodes Using a Multilayer Oxide as a Composite Cathode
作者单位
陕西科技大学 电气与信息工程学院,陕西,西安710021
摘要
制备了一种采用多层氧化物复合阴极的透明OLED,器件结构为:ITO/ MoO3(10 nm) /NPB(60 nm)/Alq3(65 nm)/ Al(1 nm)/ MoO3(1 nm)/Al(X nm) /MoO3(30 nm)。所采用的复合阴极结构为MoO3/Al/ MoO3 (MAM),同时在复合阴极(MAM)与电子传输层(Alq3)中间插入一层厚度为1 nm的Al中间层,该薄Al层一方面提高了电极与有机层间界面的平整度,同时增强了电极的导电性;另一方面,在电子传输层与中间层Al薄膜之间形成了良好的欧姆接触,提高了电子的注入能力。改变MAM结构中Al的厚度,获得该透明OLEDs的最佳性能,在Al的厚度为18 nm时器件亮度最高,为2 297 cd/cm2。
Abstract
Transparent organic light emitting diodes are developed by using a multilayer oxide as a composite cathode. The device structure is ITO/ MoO3(10 nm)/NPB(60 nm)/Alq3(65 nm)/Al(1 nm)/MoO3(1 nm)/Al(X nm) /MoO3(30 nm). The composite cathode is MoO3/Al/MoO3 (MAM). A thin Al layer (1 nm) was introduced as an interlayer between the Alq3 electron transport layer and the MAM electrode. On the one hand, the thin Al layer improves the interface flatness between electrode and organic layers, while improving the conductivity of the electrode. On the other hand, electron injection was greatly improved by forming an Ohmic contact between the electron transport layer and a thin Al layer. Then the OLEDs optimum performance is obtained by changing the thickness of Al in MAM. With the Al thickness of 18 nm, the highest brightness 2 297cd/cm2 is obtained.

梁田静, 张方辉, 丁磊. 多层氧化物复合阴极透明OLED器件[J]. 液晶与显示, 2012, 27(1): 43. LIANG Tian-jing, ZHANG Fang-hai, DING Lei. Transparent Organic Light Emitting Diodes Using a Multilayer Oxide as a Composite Cathode[J]. Chinese Journal of Liquid Crystals and Displays, 2012, 27(1): 43.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!