应用激光, 2012, 32 (2): 108, 网络出版: 2012-05-22   

高温合金-不锈钢异种金属光纤激光焊接试验研究

Experimental Investigation on Fiber Laser Welding Stainless Steel 304 to Super Alloy GH3128
作者单位
北京工业大学激光工程研究院, 北京 100124
摘要
采用光纤激光对GH3128与304不锈钢进行对接焊, 研究了焊接速度、激光作用位置等工艺参数对焊缝成形及接头力学性能的影响规律。结果表明: 通过工艺参数优化, 可以获得无气孔、裂纹等缺陷的焊接接头。焊接速度较低时, 焊缝上下部的熔宽较大, 随焊接速度的提高, 焊缝下部的熔宽减小到与中部相当, 随激光作用位置向不锈钢侧靠近, 接头强度和延伸率降低。当激光作用于GH3128侧, 在焊接速度小于2 m/min时, 焊接接头拉伸试验时断于304不锈钢母材; 当焊接速度为3 m/min时, 焊缝存在未熔合, 接头强度仅为母材的37%。
Abstract
The influence of laser welding parameters, such as welding velocity and welding position, on weld shaping and mechanical properties of dissimilar SS304 and Super Alloy GH3128 was investigated. The welding experiment adopted the butt joint using fiber laser. Result shows no crack and porosity existing in weld after parameter optimization. Weld width in the top and bottom is wider than that in the middle at low welding speed. However, at high welding speed, the wider weld was only observed in the top. Mechanical tests indicate that strength and elongation decrease with welding position moving to SS304. At the welding speed of 2 m/min and welding position close to GH3128, sample fractured at base metal SS304. When the welding speed is increased to 3 m/min, the strength of the joint is only 37% of base metal. The sample fractured on the weld and the incomplete fusion was observed.

周春阳, 吴世凯, 肖荣诗. 高温合金-不锈钢异种金属光纤激光焊接试验研究[J]. 应用激光, 2012, 32(2): 108. Zhou Chunyang, Wu Shikai, Xiao Rongshi. Experimental Investigation on Fiber Laser Welding Stainless Steel 304 to Super Alloy GH3128[J]. APPLIED LASER, 2012, 32(2): 108.

本文已被 5 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!