1.06 μm InGaAs/InGaAsP量子阱半导体激光器的温度特性

Temperature Characteristic of 1.06 μm InGaAs/InGaAsP Quantum Well Laser Diode
作者单位
长春理工大学 高功率半导体激光国家重点实验室, 吉林 长春130022
摘要
研究了1.06 μm InGaAs/InGaAsP量子阱半导体激光器厘米bar模块的温度特性,测试分析了该模块的输出光功率、阈值电流、转换效率和光谱随注入电流及管芯温度变化的特性。结果表明,器件在15~55 ℃范围内所测的输出光功率由40.7 W降低到29.4 W,阈值电流由9.29 A升高到17.24 A,转换效率由54.22%降低到37.55%,光谱漂移为0.37 nm/℃,特征温度为68.6 K。实验结果表明,为保持器件性能的稳定,在实际应用过程中应该使器件的温度控制在15~25 ℃范围内。
Abstract
The temperature characteristic of 1.06 μm InGaAs/InGaAsP quantum well laser diode was studied. The output optical power, threshold current, conversion efficiency and spectra of the module were measured and analyzed when the module was operated with different current at different temperature. The results show that the modules characteristic changes with the temperature in the range of 15 ℃ to 55 ℃. The modules CW output optical power reduced from 40.7 W to 29.4 W. The threshold current increased from 9.29 A to 17.24 A. The conversion efficiency reduced from 54.22% to 37.55%. The lasing wavelength shift is 0.37 nm/℃ and the characteristic temperature is 68.6 K. The temperature of the device in the actual application process should be controlled in the range of 15 ℃ to 25 ℃ to maintain the stability of the device performance.

李再金, 芦鹏, 李特, 曲轶, 薄报学, 刘国军, 马晓辉. 1.06 μm InGaAs/InGaAsP量子阱半导体激光器的温度特性[J]. 发光学报, 2012, 33(6): 647. LI Zai-jin, LU Peng, LI Te, QU Yi, BO Bao-xue, LIU Guo-jun, MA Xiao-hui. Temperature Characteristic of 1.06 μm InGaAs/InGaAsP Quantum Well Laser Diode[J]. Chinese Journal of Luminescence, 2012, 33(6): 647.

本文已被 5 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!