采用高温熔融法和热处理工艺制作了含有GdF3纳米晶的氧氟微晶玻璃。在386 nm激发下, Dy3+掺杂氧氟微晶玻璃的发光强度明显增强, 且蓝光对黄光的发光强度比逐渐增大, 表明Dy3+已进入到GdF3纳米晶中。在980 nm激光器泵浦下, Er3+, Yb3+共掺氧氟微晶玻璃的上转换发光随着热处理温度的升高明显增强, Er3+的上转换发光出现明显的Stark分裂现象, 这亦说明Er3+已进入到GdF3纳米晶相中。通过研究上转换发光强度与泵浦功率的关系, 确定绿光上转换发光为双光子过程。
Abstract
The transparent oxyfluoride glass ceramics containing GdF3 nanocrystals were prepared by high-temperature melting and heat treatment method. Comparison with the as-prepared glass, Dy3+ doped oxyfluoride glass ceramics exhibit higher emission intensity excited at 386 nm and the intensity ratio between blue light and yellow light emission increases gradually with the heat treatment temperature, which indicates that Dy3+ ions have participated into the precipitated GdF3 nanocrystals. Under the excitation of 980 nm laser diode, the upconversion luminescence intensity increases gradually with the heat treatment temperature and the upconversion luminescence peaks appear apparent Stark splitting phenomenon, which also demonstrates Er3+ ions have entered into the precipitated GdF3 nano-crystalline phase. Based on the relationship between excited power and the upconversion intensity in Er3+,Yb3+ doped glass ceramic GC-650, two-photon absorption process was determined for the green upconversion emission of Er3+.

陈文威, 赵士龙, 陈水林, 左达先, 左伟超, 徐时清. Dy3+单掺和Er3+,Yb3+共掺氧氟微晶玻璃的发光性能[J]. 发光学报, 2012, 33(10): 1078. CHEN Wen-wei, ZHAO Shi-long, CHEN Shui-lin, ZUO Da-xian, ZUO Wei-chao, XU Shi-qing. Photoluminescence Properties in Dy3+-doped and Er3+,Yb3+ Co-doped Oxyfluoride Glass Ceramics[J]. Chinese Journal of Luminescence, 2012, 33(10): 1078.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!