紫外应力发光材料SrMgSi2O6∶Ce的制备与光谱性质研究

Ultraviolet Mechanoluminescence from SrMgSi2O6∶Ce
作者单位
1 厦门理工学院 材料科学与工程学院, 福建 厦门361024
2 中国科学院 城市环境研究所, 福建 厦门361021
摘要
采用固相烧结法制备了3种紫外应力发光材料SrMgSi2O6∶Ce0.005、SrMgSi2O6∶Ce0.005, Er0.015和Sr2MgSi2O7∶Ce0.005, Er0.015。XRD测试结果表明:SrMgSi2O6与Sr2MgSi2O7具有相同的结构, 掺杂离子的加入没有改变相结构。3种样品的荧光发射光谱很类似, 均在330~400 nm紫外波段有较宽的发射谱带。应力发光曲线的测试结果表明, 样品的应力发光强度与物体受力变化呈良好的对应关系, 证明所制备的样品可以用来检测物体的受力情况。同时, 研究了共掺杂离子以及改变基质结构对应力发光强度的影响, 结果表明发光体中陷阱数目的增加以及基质对称性的降低有利于应力发光的产生。由于所开发的样品波长在紫外区, 因而可以作为光源来激发其他颜色的光致发光材料从而实现多颜色应力发光材料的开发。
Abstract
UV mechanoluminescent (ML) phosphors SrMgSi2O6∶Ce0.005, SrMgSi2O6∶Ce0.005, Er0.015 and Sr2MgSi2O7∶Ce0.005, Er0.015 were prepared via solid state reaction. The XRD results indicate that the structure of SrMgSi2O6 is identical to that of Sr2MgSi2O7, which has a tetragonal symmetry with a space group P421m.The emission bands of three samples are similar, which consist of a broad band with two peaks centered at 349 and 371 nm, caused by the f-d electron transition of Ce3+ ions. The ML results show that the ML intensities of these samples are well depended on the stress, indicating that these ML materials can be potentially used as sensors to detect the stress distribution of an object. Furthermore, the ML intensity of SrMgSi2O6∶Ce0.005, Er0.015 is obviously higher than those of SrMgSi2O6∶Ce0.005 and Sr2MgSi2O7∶Ce0.005, Er0.015. The obtained results suggest that the trap and the worse symmetry of crystal structure are responsible for the higher ML intensity of SrMgSi2O6∶Ce0.005, Er0.015. Because of the UV emission of this material, it can be used as the excitation source to irradiate other color phosphors and then the various colors ML can be realized.

付晓燕, 房立均, 付海霞, 张洪武. 紫外应力发光材料SrMgSi2O6∶Ce的制备与光谱性质研究[J]. 发光学报, 2013, 34(8): 1006. FU Xiao-yan, FANG Li-jun, FU Hai-xia, ZHANG Hong-wu. Ultraviolet Mechanoluminescence from SrMgSi2O6∶Ce[J]. Chinese Journal of Luminescence, 2013, 34(8): 1006.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!