激光与光电子学进展, 2014, 51 (2): 021601, 网络出版: 2014-01-21   

激光重熔对CoCrAlYTa涂层组织及氧化性能的影响

Effect of Laser Remelting on Mircrostructure and Properties of CoCrAlYTa Coating
作者单位
1 北京科技大学材料科学与工程学院, 北京 100083
2 核工业标准化研究所, 北京 100091
摘要
采用等离子喷涂工艺在Co基合金表面制备CoCrAlYTa-Al2O3-ZrB2复合涂层,并采用激光重熔工艺对涂层进行处理。通过扫描电镜(SEM)、和X射线衍射仪(XRD)对重熔前后试样进行检测,分析涂层的微观结构及物相组成,同时对涂层进行高温氧化实验,比较重熔前后试样的性能。结果表明,激光重熔消除了等离子喷涂层的片层状结构、孔隙等缺陷,涂层致密性有很大提高;激光重熔层截面显微硬度从平均899.47 HV提高到929.484 HV;激光重熔层氧化增重速率约为等离子喷涂层的1/6,且氧化膜均匀致密,有效阻止氧化的进一步进行,从而大大提高涂层的抗氧化性能。
Abstract
CoCrAlYTa-Al2O3-ZrB2 composite coating is deposited on the Co base alloy surface by laser remelting. The microstructure, phase and micro-hardness are studied using scanning electron microscope (SEM) and X-ray diffractometer (XRD).The high temperature oxidation test is conducted. It is found that the defects of as-sprayed coating like lamellar stacking microstructure and pores are eliminated by laser remelting, and the remelted coating possesses a denser microstructure. The micro-hardness of the remelted coating at the cross section is promoted from an average of 899.47 HV to 929.484 HV. The properties of oxidation resistance are significantly improved. The increased mass of the remelted coating is 1/6 of that of the clad coating, and the oxide film of the remelted coating is homogeneous.

柯婷婷, 樊自拴, 张宏伟. 激光重熔对CoCrAlYTa涂层组织及氧化性能的影响[J]. 激光与光电子学进展, 2014, 51(2): 021601. Ke Tingting, Fan Zishuan, Zhang Hongwei. Effect of Laser Remelting on Mircrostructure and Properties of CoCrAlYTa Coating[J]. Laser & Optoelectronics Progress, 2014, 51(2): 021601.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!