中国激光, 2015, 42 (2): 0206003, 网络出版: 2015-01-09
大尺寸连熔N31型掺钕磷酸盐激光玻璃的性能研究
Properties of Large Size N31 Nd:Phosphate Laser Glass Prepared by Continuous Melting
光学制造 激光钕玻璃 连续熔炼工艺 损耗 增益系数 optical fabrication Nd-doped laser glass continuous melting technology optical loss gain coefficient
摘要
报道了磷酸盐激光钕玻璃的连续熔炼线,以及采用连续熔炼工艺获得的400 mm 口径N31 钕玻璃的主要性能。连熔所制备的N31-35 钕玻璃的掺杂离子浓度为3.47(±0.02)×1020 cm-3;1053 nm 处的折射率为1.5336±0.0005;400 nm 处的吸收系数平均值为0.098 cm-1;1053 nm 处的激光波长损耗为0.13~0.15% cm-1;3000 cm-1 处的吸收系数平均值为0.83 cm-1。400 mm 口径连熔N31 钕玻璃的透射波前畸变在633 nm 处小于λ/3 波长。采用1053 nm、脉冲为3 ns激光作用下连熔钕玻璃的体破坏阈值大于40 J/cm2。结果表明,在N31 钕玻璃的连续熔炼工艺中,除铂金和除水都取得了很好的效果。
Abstract
The continuous melting technology is reported. The 400 mm aperture N31 Nd:phosphate laser glass prepared from continuous melting technology is fabricated. The main properties of N31-35 glass have been disclosed. Its Nd3 + ion concentration is 3.47 (± 0.02)× 1020 cm-3. The refractive index at 1053 nm is 1.5336 ±0.0005. The absorption coefficients at 400 nm and 3000 cm-1, the laser wavelength loss at 1053 nm are 0.098 cm-1 and 0.83 cm-1, 0.13~0.15% cm-1, respectively. The PV value of transmitted wavefront is less than λ/3 at 633 nm. Its bulk damage threshold with 1053 nm, 3 ns pulse laser is larger than 40 J/cm2. The results indicate that the dehydration and platinum particle removing processes are very effective during the continuous melting.
唐景平, 胡丽丽, 陈树彬, 陈伟, 王标, 翁泽安, 徐永春, 陈尤阔, 邹兆松, 胡俊江, 温磊, 李顺光. 大尺寸连熔N31型掺钕磷酸盐激光玻璃的性能研究[J]. 中国激光, 2015, 42(2): 0206003. Tang Jingping, Hu Lili, Chen Shubin, Chen Wei, Wang Biao, Weng Zean, Xu Yongchun, Chen Youkuo, Zou Zhaosong, Hu junjiang, Wen Lei, Li Shunguang. Properties of Large Size N31 Nd:Phosphate Laser Glass Prepared by Continuous Melting[J]. Chinese Journal of Lasers, 2015, 42(2): 0206003.