红外线治疗仪中宽波段带通滤光片的研究

Study and Fabrication of Broad Band-pass Filters in Infrared Therapy Apparatus
作者单位
长春理工大学 光电工程学院, 长春 130022
摘要
研究了一种用于红外线治疗仪的新型滤光片.该滤光片通过对红外线治疗仪光源所发出的光进行选择性滤波, 能够降低部分波段光的承载能量, 提高治疗仪的安全使用性能.针对红外线治疗仪对滤光片的使用要求, 选择Ti3O5和SiO2作为高低折射率材料, 采用电子束加热蒸发方式, 配合离子辅助淀积技术, 利用石英晶控控制法对膜层厚度进行监控, 通过反复优化各项工艺参量, 制备出在600-1 200 nm波段平均透过率高于92%, 300-550 nm、1 270-2 000 nm波段平均透过率低于2%的宽波段带通滤光片.研究中运用 “拆分技术要求”的设计思想, 对颜色片进行双面镀制, 解决了单面膜层过厚难以制备的问题, 降低了制备难度, 易于批量生产.测试结果表明, 该滤光片满足使用要求.
Abstract
Design and manufacture of a new type of filters which meet the infrared therapy apparatus needs. By selectively filtering for the light of the infrared light emitted by the therapy apparatus, reducing the portion of the band light carrier energy, improving the safety performance of the therapy apparatus. Based on the use requirements of the filters to infrared therapy apparatus, chose Ti3O5 and SiO2 as high and low refractive index materials respectively. Thin films were prepared through electron beam evaporation method and ion-assisted deposition technique, and the thickness of the filter was controlled using crystal-controlled.By repeatedly optimizing technical parameters, the band-pass filter was prepared. The average transmittance of the filter is higher than 92% at the band of 600-1200nm, the average transmittance of the broad band-pass filter is less than 2% at the band of 300-550nm and1270nm-2000nm. To solve the problem of the single sided film was too thick to prepared. Based on the concept of splitting technical requirements, the double-sided of the color filter were coated. The results show that the difficulty of preparation are reduced, and filters can be easily manufactured in a large scale, the filter meets the actual requirements.

刘冬梅, 刘爽, 付秀华, 张静, 何松霖. 红外线治疗仪中宽波段带通滤光片的研究[J]. 光子学报, 2015, 44(3): 0331001. LIU Dong-mei, LIU Shuang, FU Xiu-hua, ZHANG Jing, HE Song-lin. Study and Fabrication of Broad Band-pass Filters in Infrared Therapy Apparatus[J]. ACTA PHOTONICA SINICA, 2015, 44(3): 0331001.

本文已被 4 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!