微观缺陷对材料损伤阈值的影响分析

Analysis of laser-induced damage threshold influenced by micro-defects
作者单位
1 四川大学 电子信息学院, 成都 610065
2 中国工程物理研究院 流体物理研究所, 四川 绵阳 621900
摘要
为了研究材料表面高频缺陷对损伤阈值的影响规律,针对典型表面圆锥凸起状表面缺陷建立了三维分析模型,使用有限元算法计算了两种不同波长激光辐照下,表面缺陷周围的电场变化规律.基于激光诱导材料产生损伤的场效应理论,对缺陷存在条件下材料的损伤阈值进行了定量计算.结果表明,缺陷的存在会对电场产生明显的放大效应,这将直接导致损伤阈值的下降;损伤阈值与缺陷高度成反比关系,与入射波长成正比关系;缺陷导致的损伤阈值下降幅度会随脉宽增加先减小后增大,当入射波长分别为351 nm和1064 nm时,缺陷导致的损伤阈值下降幅度分别在脉宽为1.80 ps和15.80 ps处最小.
Abstract
In order to study the effect of the defects on damage threshold of the surface,we modeled a classical three-dimension defect which is similar to the circular cone protuberance and calculated the electric field around this kind of defects by finite-difference method.Based on the field effect theory we calculated the damage thresholds of surfaces with different size defects.It can be got that the electric fields were amplified obviously,which directly leads to lower damage thresholds.The damage threshold increases as incident wavelength increases and the height of defect decreases.The reduction of damage threshold caused by defect decreases first and then increases with the pulse increasing.The damage threshold owns a minimum at 1.80 ps and 15.80 ps when the wavelength is respectively 351 nm and 1064 nm.

李风雨, 刘国栋, 杜立峰, 罗银川, 张蓉竹. 微观缺陷对材料损伤阈值的影响分析[J]. 强激光与粒子束, 2015, 27(6): 061021. Li Fengyu, Liu Guodong, Du Lifeng, Luo Yinchuan, Zhang Rongzhu. Analysis of laser-induced damage threshold influenced by micro-defects[J]. High Power Laser and Particle Beams, 2015, 27(6): 061021.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!