新型Fe 基非晶复合涂层的制备及性能研究
Investigation on Fabrication and Properties of N-Doped Fe-Based Amorphous Composite Coatings on High Strength Steel
激光光学 激光熔覆 Fe基非晶复合涂层 硬度 耐磨损性 耐蚀性 laser optics laser cladding Fe- based amorphous composite coating hardness wear resistance corrosion resistance
摘要
利用IPG YLS4000 光纤激光器,采用激光熔覆工艺在某高强钢基体上制备了一种新型含氮Fe 基非晶复合涂层。通过X 射线衍射仪物相分析发现,在3种不同激光工艺下制备的涂层在非晶基体上出现了不同含量的晶化相,分别对3种工艺下制备的涂层与基体材料的硬度、耐磨及耐蚀性能进行了测试分析。结果表明,与基体材料相比,3种涂层的硬度、耐磨及耐蚀性均有明显提高,其中在1.5 kW 激光功率、180 mm/min扫描速度条件下制备的涂层非晶含量最高,表现出最好的性能。研究认为合适的工艺才能制备出性能优良的涂层,涂层中非晶相含量的增加能够明显改善涂层的性能。
Abstract
With the IPG YLS4000 optical fiber laser, N-doped Fe-based amorphous composite coatings are prepared on a high strength steel substrate by three laser processes. The three coatings show amorphous structure with crystalline phase on them. The hardness, wear resistance and corrosion resistance of the coatings are evaluated, indicating that the coatings have higher hardness, better wear resistance and corrosion resistance than substrate. The coating 2 fabricated under laser power of 1.5 kW and laser beam scanning speed of 180 mm/min has the highest amorphous phase content among the three coatings, and it also exhibits the best performance compared with the other two coatings. The results show that proper laser process parameters are important and coatings with higher amorphous phase content have better properties.
侯纪新, 章顺虎, 周巍, 王晓南, 蒋小舟, 朱广江. 新型Fe 基非晶复合涂层的制备及性能研究[J]. 中国激光, 2015, 42(11): 1103009. Hou Jixin, Zhang Shunhu, Zhou Wei, Wang Xiaonan, Jiang Xiaozhou, Zhu Guangjiang. Investigation on Fabrication and Properties of N-Doped Fe-Based Amorphous Composite Coatings on High Strength Steel[J]. Chinese Journal of Lasers, 2015, 42(11): 1103009.