ZnO/ZnFe2O4复合纳米粒子的制备及其特性研究

Growth and properties of ZnO/ZnFe2O4 nanoparticles
作者单位
1 长春理工大学 高功率半导体激光国家重点实验室,吉林 长春 130022
2 中国科学院长春光学精密机械与物理研究所,吉林 长春 130033
摘要
利用水热法制备了ZnO/ZnFe2O4纳米复合粒子。用扫描电子显微镜(SEM)、X射线衍射(XRD)、光致发光光谱(PL)对退火前后的ZnO/ZnFe2O4纳米粒子进行表征。研究结果表明,退火后的ZnO/ZnFe2O4纳米复合粒子表现出更好的形貌和晶体质量,主要由六角纤锌矿结构的ZnO和立方结构的ZnFe2O4构成。PL光谱显示,退火后ZnO近带边的发光强度明显降低,这是由于ZnO/ZnFe2O4形成了Ⅱ型能带结构实现了光生载流子分离的结果。对其光催化特性也进行了研究,光照时间为3 h,退火后的ZnO/ZnFe2O4纳米复合粒子表现出更优秀的光催化活性,降解甲基橙的效率可达50.48%。另外,还对其磁性进行了研究,室温条件下,纳米复合粒子表现为顺磁性,而经过退火处理后表现出铁磁性。因此,ZnO/ZnFe2O4纳米复合粒子经退火后具备磁性光催化剂性能,有一定的发展前景。
Abstract
ZnO/ZnFe2O4 nanoparticles were synthesized by hydrothermal and annealed method. X-ray diffraction(XRD), scanning electron microscopy(SEM) and photoluminescence(PL) spectroscopy were used to characterize the synthesized and annealed ZnO/ZnFe2O4 nanoparticles. The results indicate that the synthesized nanoparticles are mainly composed of hexagon wurtzite ZnO and cubic ZnFe2O4, and the crystal quality is improved by annealing treatment. It is observed that the intrinsic photoluminescence attributed to the recombination of photogenerated carriers of ZnO was obviously weakened after annealing process, which confirms that a ZnO/ZnFe2O4 heterojunction was formed which could improve the separation of photogenerated carriers. Photocatalytic test′s results show the photocatalytic activity of the annealed ZnO/ZnFe2O4 nanoparticles is better than the synthesized, and the photocatalytic degradation ratio of MO is 50.48% under 3 hours′ UV-illumination. The magnetic properties of the annealed ZnO/ZnFe2O4 were also investigated, the synthesized nanoparticles were paramagnetic at room temperature, and the annealed nanoparticles were ferromagnetic. In conclusion, the annealed ZnO/ZnFe2O4 nanoparticles may have a great potential in the magnetic photocatalytic fields.

高娴, 贾慧民, 方铉, 刘鹤, 唐吉龙, 房丹, 王双鹏, 赵海峰, 李金华, 方芳, 楚学影, 王菲, 王晓华, 徐莉, 马晓辉, 魏志鹏. ZnO/ZnFe2O4复合纳米粒子的制备及其特性研究[J]. 红外与激光工程, 2015, 44(7): 2110. Gao Xian, Jia Huimin, Fang Xuan, Liu He, Tang Jilong, Fang Dan, Wang Shuangpeng, Zhao Haifeng, Li Jinhua, Fang Fang, Chu Xueying, Wang Fei, Wang Xiaohua, Xu Li, Ma Xiaohui, Wei Zhipeng. Growth and properties of ZnO/ZnFe2O4 nanoparticles[J]. Infrared and Laser Engineering, 2015, 44(7): 2110.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!