基体预热对激光沉积修复GH4169合金性能的影响

Effect of Substrate Preheating on Property of GH4169 Alloys Repaired by Laser Deposition
作者单位
1 沈阳航空航天大学航空制造工艺数字化国防重点学科实验室, 辽宁 沈阳 110136
2 中国航空工业沈阳黎明航空发动机(集团)有限责任公司焊接研究所, 辽宁 沈阳 110043
3 沈阳工业大学机械工程学院, 辽宁 沈阳 110870
摘要
研究了基体预热对激光沉积修复GH4169合金试样的残余应力、组织和拉伸性能的影响。结果表明,基体预热至300 ℃的GH4169合金试样,残余应力x向分力σx的平均降幅为59.4 MPa,降低了11.7 %。残余应力y向分力σy的平均降幅为189.7 MPa,降低了44.6 %。沉积层枝晶间析出Laves相呈现颗粒状的碎化现象。抗拉强度和屈服强度与未预热的修复试样基本一致,断后伸长率为12.3%,提高了近一倍,达到锻件标准。试验表明基体预热可有效提高激光沉积修复GH4169合金的室温拉伸性能。
Abstract
The effect of substrate preheating process on the residual stress, microstructure, and tensile property of GH4169 alloy samples repaired by laser deposition is studied. The results show that when the substrate is preheated to 300 ℃, as for the GH4169 alloy sample, the average decrease in amplitude of the residual stress along x direction (σx) is 59.4 MPa, which is reduced by 11.7%. The average decrease in amplitude of σy along y direction is 189.7 MPa, which is reduced by 44.6%. The Laves phase of the interdendritic precipitation in deposition layers presents a granular fragmentation phenomenon. Both the tensile strength and yield strength are basically equivalent to those of repaired samples without preheating, and the elongation rate is 12.3%, which is a onefold increase. These indicate the standard of forging is reached. The experimental results indicate that substrate preheating can effectively improve the tensile property of GH4169 alloys repaired by laser deposition at room temperature.

卞宏友, 赵翔鹏, 曲伸, 王世杰, 杨光, 钦兰云, 王维. 基体预热对激光沉积修复GH4169合金性能的影响[J]. 中国激光, 2016, 43(7): 0702003. Bian Hongyou, Zhao Xiangpeng, Qu Shen, Wang Shijie, Yang Guang, Qin Lanyun, Wang Wei. Effect of Substrate Preheating on Property of GH4169 Alloys Repaired by Laser Deposition[J]. Chinese Journal of Lasers, 2016, 43(7): 0702003.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!