氧化锆陶瓷板激光切割熔化物颗粒形态研究

Melt particles morphology during laser cutting zirconia ceramic
作者单位
大连理工大学 机械工程学院,辽宁 大连 116024
摘要
本文设计了一套加工装置,对氧化锆陶瓷板激光切割的熔化物颗粒进行收集,并采用Imagine-Pro Pluse(IPP)图像处理软件对熔化物颗粒的形态(数量、形状、平均直径、标准差及其分布情况)进行研究。通过气熔比控制方法,对板厚分别为08 mm、1 mm、15 mm、3 mm的氧化锆陶瓷板进行激光切割实验。实验结果表明: 不同板厚参数下,球形熔化物颗粒所占百分比范围从9921%降到8981%,圆饼形从079%升至744%,哑铃形从0升至275%。随着板厚的增加,圆饼形和哑铃形颗粒所占百分比增大,球形颗粒所占百分比降低,球形颗粒平均直径和标准差随之增大,切面粗糙度由2287 μm增加到5946 μm。建立了熔化物去除几何模型,阐述了熔化物颗粒与切割质量的关系,球形颗粒所占的百分比越大,平均直径和标准差越小,切割质量越好,最终获得质量较高切割样件。
Abstract
A set of processing device is designed to collect the melt particles during laser cutting zirconia ceramic. The melt particles morphology including quantity, shape, mean dimeter, standard deviation, and distribution are studied using the image processing software of Imagine-Pro Pluse(IPP). Various cutting experiments with different ceramic thicknesses(08 mm, 10 mm, 15 mm and 3 mm) are taken based on controlling of vapor-to-melt ratio. Results of IPP observation show that, with the ceramic thickness increased, the percentage of spherical molten particles is declined from 9921% to 8981%, while the cakey and dumbbell shaped molten particles are ascended from 079% to 744% and 0 to 275% respectively, and the mean and standard deviation of spherical melt particles diameter also are enlarged. Simultaneously, with the increasing of mean and standard deviation of spherical particle diameter, the roughness of kerf surface is deteriorated from 2287 μm to 5946 μm. The establishment of geometric model reveals the connection between the form of removal molten particles and cutting quality. The larger the percentage of spherical molten particles, the smaller the mean diameter and standard deviation, and then the better the cutting quality. The high quality cutting sheet is achieved finally.

吴迪, 王续跃. 氧化锆陶瓷板激光切割熔化物颗粒形态研究[J]. 中国光学, 2016, 9(5): 554. WU Di, WANG Xu-yue. Melt particles morphology during laser cutting zirconia ceramic[J]. Chinese Optics, 2016, 9(5): 554.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!