氮掺入对N型纳米硅薄膜微观结构及光电特性影响

Effect of the Nitrogen Incorporation on the Microstructure and Photoelectric Properties of N Type Nanocrystalline Silicon Thin Films
作者单位
北京航空航天大学物理科学与核能工程学院, 凝聚态和材料物理中心, 北京 100191
摘要
采用等离子体增强化学气相沉积技术(PECVD)通过改变NH3流量制备出不同含氮量N型富硅氮化硅硅薄膜。 利用Raman散射、 红外吸收、 紫外-可见光分光光度计及暗态I-V测量等技术分析了氮掺入对薄膜微观结构以及光电特性的影响。 结果显示, 随着NH3的增加, 薄膜由微晶硅向纳米硅结构转变, 薄膜中晶粒尺寸减少, 晶化度降低, 微观结构有序性降低, 所对应薄膜光学带隙增大, 而带尾分布变窄。 同时, 红外吸收谱分析表明, Si—N键合密度增加, P掺杂受阻。 暗态I-V测量显示, 薄膜电导率随着NH3掺入整体较微晶硅降低, 但随NH3增加, 电导率受到迁移率和载流子浓度等特征共同作用先降低后变大, 揭示了影响薄膜电导率的机制存在一定的竞争, 然而过高的非晶网络结构将增大载流子的复合导致薄膜电导率显著降低。
Abstract
N type silicon-rich nanocrystalline-SiNx∶H films were prepared by plasma enhanced chemical vapor deposition technique by changing NH3 flow rate. The effect of nitrogen incorporation on the microstructure and photoelectric properties of the thin films were characterized by Raman, Fourier transform infrared spectroscopy, ultraviolet-visible absorption spectra, and Hall effect measurement. The results indicated that with the increasing NH3, a phase transition from microcrystalline to amorphous silicon occured. Transmission electron microscope observation revealed that the size of silicon quantum dots could be adjusted by varying the flow rate of NH3. The microstructure order of the films reduced with increasing the flow rate of NH3, while the optical band gap increased, and the optical band tail became narrow. Meanwhile, Si—N bonds density increased and P doping was blocked. I-V testing results showed that with increasing NH3, the conductivity of films first decreased compared with nanocrystalline-Si and then increased. These behaviors reveal a competition in the mechanisms controlling the conductivity. However, with further increasing NH3, the conductivity decreased significantly due to rapid carrier recombination on the amorphous net structure.

马登浩, 张维佳, 罗瑞盈, 刘承月, 蒋昭毅, 马晓波, 范志强. 氮掺入对N型纳米硅薄膜微观结构及光电特性影响[J]. 光谱学与光谱分析, 2017, 37(2): 629. MA Deng-hao, ZHANG Wei-jia, LUO Rui-ying, LIU Cheng-yue, JIANG Zhao-yi, MA Xiao-bo, FAN Zhi-qiang. Effect of the Nitrogen Incorporation on the Microstructure and Photoelectric Properties of N Type Nanocrystalline Silicon Thin Films[J]. Spectroscopy and Spectral Analysis, 2017, 37(2): 629.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!