为了研究表激光织构化对机械零件接触面的摩擦性能影响, 采用Nd∶YAG脉冲激光在钢盘表面形成了具有一定直径、间距和密度的微坑型织构阵列, 在环/盘式摩擦试验机上进行了摩擦学性能测试。结果表明,微坑的深度和直径随脉冲次数增加而增大, 调整微坑参量(直径和间距)可以获得不同密度的织构阵列, 密度为8％~10%范围内的试样具有最低的摩擦因素(0.055~0.06)和磨损率(5.2×10-16m3/(N·m)); 通过曲线拟合, 得到摩擦磨损性能随织构密度变化的趋势。该研究获得了具有最佳摩擦学性能的参量, 能提高机械的使用效率和使用寿命。

In order to study the effect of laser micro-modeling on the friction performance of mechanical parts, Nd∶YAG pulsed laser was used to form a micro pit texture array with certain diameter, spacing and density on the surface of a steel plate. The tribological performance was tested on ring/disc friction tester. The results show that the depth and diameter of micro pits increase with the increase of pulse number. The texture arrays with different densities can be obtained by adjusting the parameters (diameter and spacing). The specimen with a density of 8%~10% has the lowest friction factor of 0.055~0.06 and the lowest wear rate of 5.2×10-16m3/(N·m). The trend of the friction and wear performance with the change of texture density is obtained by curve fitting. The study obtains the parameters of the best tribological properties and can improve the mechanical efficiency and service life.