Bi3+或Sm3+掺杂对NaGd(WO4)2∶Eu3+荧光粉结构和发光性质的影响

Influence of Bi3+ or Sm3+ Doping on Structure and Luminescence Properties of NaGd(WO4)2∶Eu3+ Phosphors
作者单位
河北大学 化学与环境科学学院, 河北 保定071002
摘要
采用水热法制备了白光LED用NaGd0.95-x(WO4)2∶0.05Eu3+,xBi3+(x=0, 0.02, 0.04, 0.06, 0.08)和NaGd0.95-y(WO4)2∶0.05Eu3+,ySm3+(y=0, 0.01, 0.02, 0.03, 0.04)系列红色荧光粉, 通过X射线衍射仪、扫描电子显微镜及荧光分光光度计等表征手段分析了样品的物相结构、颗粒形貌以及发光性质。结果表明: 少量离子掺杂对NaGd(WO4)2的晶体结构影响较小, 样品均为四方晶系、白钨矿结构的纯相; 颗粒形貌呈四方盘状, 且粒度均匀, 分散性良好, Bi3+或Sm3+的引入使颗粒尺寸由原来的4 μm分别增加至5 μm和6 μm。该系列荧光粉均可被近紫外光(394 nm)有效激发, 其最强发射峰位于614 nm处, 归属于Eu3+的5D0→7F2电偶极跃迁。掺杂适量的Bi3+或Sm3+可有效提高NaGd0.95(WO4)2∶0.05Eu3+荧光粉的发光强度和红光的色纯度, 其中Sm3+的引入对其影响更为明显。
Abstract
A series of red phosphors NaGd0.95-x(WO4)2∶0.05Eu3+,xBi3+(x=0, 0.02, 0.04, 0.06, 0.08)and NaGd0.95-y(WO4)2∶0.05Eu3+,ySm3+(y=0, 0.01, 0.02, 0.03, 0.04)were synthesized via hydrothermal process. The structure, morphology and luminescent properties of the samples were characterized by X-ray diffraction, scanning electron microscope and fluorescence spectrophotometer, respectively. The results indicate that the crystal structure of NaGd(WO4)2 is almost not changed by doping a small amount of ions, and all samples are tetragonal scheelite-type pure phase. The particles are square plate in shape, relatively uniform and well dispersive. With the introduction of Bi3+ or Sm3+, the particle size increases from the original 4 μm to 5 μm and 6 μm, respectively. The series of phosphors can be effectively excited under near-UV (at 394 nm), and the strongest emission peak is located at 614 nm which corresponds to the 5D0→7F2 transition of Eu3+. In addition, doping with an appropriate amount of Bi3+ or Sm3+ can improve the luminescence intensity and red-light purity of NaGd0.95(WO4)2∶0.05Eu3+ phosphors, especially for Sm3+.

翟永清, 赵鑫, 杨帅, 孙庆琳, 邓德芮, 胡正磊, 丁士文, 苗曼红. Bi3+或Sm3+掺杂对NaGd(WO4)2∶Eu3+荧光粉结构和发光性质的影响[J]. 发光学报, 2017, 38(8): 987. ZHAI Yong-qing, ZHAO Xin, YANG Shuai, SUN Qing-lin, DENG De-rui, HU Zheng-lei, DING Shi-wen, MIAO Man-hong. Influence of Bi3+ or Sm3+ Doping on Structure and Luminescence Properties of NaGd(WO4)2∶Eu3+ Phosphors[J]. Chinese Journal of Luminescence, 2017, 38(8): 987.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!