光学学报, 2017, 37 (9): 0931001, 网络出版: 2018-09-07   

铝纳米颗粒表面等离子体共振峰可控性研究 下载: 1091次

Controllability Study of Surface Plasmon Resonance Spectra of Aluminium Nanoparticles
作者单位
1 上海理工大学光电信息与计算机工程学院, 上海 200093
2 上海市现代光学系统重点实验室, 上海 200093
3 教育部光学仪器与系统工程中心, 上海 200093
摘要
在石英基底上制备了铝(Al)薄膜,同时加热烘烤制备了Al纳米颗粒,研究了不同厚度的Al纳米颗粒的吸收特性。结果表明,随着烘烤温度的上升,Al薄膜的粗糙度越来越大;当温度达到300 ℃时,Al薄膜完全转化成Al纳米颗粒。在300 ℃的烘烤温度下,当膜厚从5 nm增加到25 nm时,薄膜的共振吸收峰红移40 nm。这种制备Al纳米颗粒的工艺简单、省时、成本低、效率高。
Abstract
Aluminium (Al) thin films are prepared on the quartz substrate, and meanwhile Al nanoparticles are obtained by baking the Al thin films. The absorption property of Al nanoparticles with different thicknesses are studied. The results show that the roughness of Al thin films increases with the increase of baking temperature. When the baking temperature reaches 300 ℃, the Al thin films are completely transformed into Al nanoparticles. When the film thickness varies from 5 nm to 25 nm, the redshift of the thin film resonance absorption peak is 40 nm at the baking temperature of 300 ℃. This fabrication process of Al nanoparticles is simple, time-saving, low-cost, and high-efficiency.

马守宝, 刘琼, 钱晓晨, 洪瑞金, 陶春先. 铝纳米颗粒表面等离子体共振峰可控性研究[J]. 光学学报, 2017, 37(9): 0931001. Shoubao Ma, Qiong Liu, Xiaochen Qian, Ruijin Hong, Chunxian Tao. Controllability Study of Surface Plasmon Resonance Spectra of Aluminium Nanoparticles[J]. Acta Optica Sinica, 2017, 37(9): 0931001.

本文已被 7 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!