电泳沉积法制备的Zn1-xCuxO薄膜的结构及阻变性能

Structure and Resistive Switching Behaviors of Zn1-xCuxO Films Derived by Electrophoretic Deposition
作者单位
华南理工大学 材料科学与工程学院, 广东 广州 510640
摘要
采用电泳沉积法在FTO导电玻璃基片上制备Zn1-xCuxO薄膜, 并对其微观结构、光致发光谱、伏安特性、保持特性和转换电压分布进行探讨。PL谱表明, Cu掺杂在禁带中引入深受主能级, 降低氧空位浓度, 导致ZnO薄膜的紫外发光、蓝光发光和绿光发光峰强度降低。所得薄膜的晶粒细小、致密、均匀, 具有稳定的双极性阻变特性, 开关比Roff/Ron最高达到105, 其低阻态(LRS)和高阻态(HRS)的阻变机理分别符合欧姆定律和空间电荷限制传导理论。器件经100次循环测试后开关比无明显变化, 呈现出较为良好的抗疲劳特性。Cu掺杂对LRS影响不大, 但显著改善了HRS的分散性以及转换电压VSET的分散性。当Cu掺杂量x=0.04时, 器件表现出良好的综合性能: Roff≈106 Ω, Roff/Ron≈104, VSET介于0.4~3.03 V之间。
Abstract
Zn1-xCuxO films were fabricated on FTO substrates by electrophoretic deposition. The microstructure, PL spectra, I-V characteristics, retention measurement and switching voltage distribution were investigated. PL spectra indicate that Cu doping introduces deep acceptor level in the bandgap and decreases the concentration of oxygen vacancy, which result in the decreasing intensity of ultraviolet, blue and green luminescence. The deposited films are dense and uniform, and exhibit bipolar resistive switching behaviors with a high OFF/ON ratio of 105. The resistive switching behaviors are governed by Ohms law in the LRS and space charge limited conduction (SCLC) in the HRS, respectively. Good endurance characteristics can be retained after 100 switching cycles without any obvious fluctuation in Roff/Ron ratio. Cu2+ doping has little influence on low resistance state (LRS), but decreases the dispersion in high resistance state (HRS) and switching voltage VSET. When Cu doping content x=0.04, the devices show good properties: Roff≈106 Ω, Roff/Ron≈104, and the value of VSET is 0.4-3.03 V.

李嘉川, 何新华, 樊娇娇. 电泳沉积法制备的Zn1-xCuxO薄膜的结构及阻变性能[J]. 发光学报, 2017, 38(5): 594. LI Jia-chuan, HE Xin-hua, FAN Jiao-jiao. Structure and Resistive Switching Behaviors of Zn1-xCuxO Films Derived by Electrophoretic Deposition[J]. Chinese Journal of Luminescence, 2017, 38(5): 594.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!