高氮钢复合焊接电弧能量对焊接接头性能影响

Effect of Arc Energy on Performance of Welded Joint with High Nitrogen Steel
作者单位
长春理工大学机电工程学院, 吉林 长春 130022
摘要
以8 mm厚的高氮钢板为试验材料, 采用额定功率为4 kW的 Nd:YAG固体激光器对其进行了激光-电弧复合焊接, 研究了不同电弧能量对焊接接头性能的影响。研究表明, 随着电弧能量的增加, 焊接表面质量有所提高; 焊缝的熔深及熔宽随电弧能量的增加而增大, 且熔深较熔宽增加更明显, 热影响区范围随电弧能量增加而增大; 随着电弧能量的增加, 熔池熔滴过渡由滴状过渡转变为射流为主、射滴为辅的过渡形式; 焊接接头的硬度值随着电弧能量的增加呈整体下降趋势, 且造成硬度下降的原因是焊接接头的氮含量随热输入的增加而降低。
Abstract
The Nd:YAG solid-state lasers with rated power of 4 KW were laser-arc hybrid welding with high nitrogen steel plate with 8mm thickness as the test material,the effects of different arc energy on the performance of welded joints were studied.By means of this,With the increase of arc energy, the welding surface quality has improved;the weld penetration and the width increase with the increase of the arc energy, and the penetration depth is more obvious than the melting width, and the heat affected zone increases with the increase of the arc energy;with the increase of arc energy, the droplet transfer of molten pool is changed from droplet transition to jet, and the transition form is the auxiliary form;the hardness of the welded joint decreases as the arc energy increases, and the reason for the decrease in hardness is that the nitrogen content of the welded joint decreases with increasing heat input.

辛秀成, 张今捷, 黄根哲, 张宏, 王金钢. 高氮钢复合焊接电弧能量对焊接接头性能影响[J]. 应用激光, 2017, 37(5): 668. Xin Xiucheng, Zhang Jinjie, Huang Genzhe, Zhang Hong, Wang Jingang. Effect of Arc Energy on Performance of Welded Joint with High Nitrogen Steel[J]. APPLIED LASER, 2017, 37(5): 668.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!