利用吡啶添加剂提高钙钛矿太阳能电池的光伏性能

Improvement of The Performance of Planar Heterojunction Perovskite Solar Cells by Using Pyridine as Additive
作者单位
1 天津理工大学 显示材料与光电器件教育部重点实验室, 天津 300384
2 天津市光电显示材料与器件重点实验室, 天津理工大学 材料科学与工程学院, 天津 300384
3 天津大学 化工学院, 天津 300072
4 中国电子科技集团第18研究所, 天津 300384
摘要
研究了吡啶作为添加剂对一步法制备甲胺铅碘钙钛矿太阳能电池光电性能的影响。利用SEM、AFM、XRD、UV-Vis、PL等手段研究了不同吡啶掺杂浓度对制备的CH3NH3PbI3薄膜的表面形貌、结晶度和光学性能的影响。研究结果表明: 少量的吡啶掺杂可以提高钙钛矿薄膜的覆盖率及降低薄膜的表面粗糙度。当在CH3NH3PbI3前驱体溶液中添加体积分数为1%的吡啶时, 制备的钙钛矿太阳能电池的能量转换效率达到7.33%, 而未加吡啶的对比器件效率仅为1.01%。进一步添加吡啶会导致钙钛矿材料的降解。
Abstract
An efficient one-step solution method was demonstrated to prepare CH3NH3PbI3 perovskite solar cells by adding pyridine to the precursor solution. The film morphology, crystallinity, and optical properties of CH3NH3PbI3 perovskite films were investigated by SEM, AFM, XRD, UV-Vis and PL. The results show that the perovskite film properties (coverage of perovskite films and surface morphology) can be manipulated by incorporating a small amount of pyridine. The adding of pyridine is helpful to obtain a smooth, continuous and dense morphology. With the optimized pyridine volume fraction of 1%, the power conversion efficiency of 7.33% with Jsc of 14.64 mA/cm2, Voc of 0.82 V, and FF of 0.61 is obtained for the planar device structure. By contrast, the power conversion efficiency of the device without pyridine is only 1.01%. However, the further increase of the content of pyridine can result in the decomposition of perovskite, because the pyridine can easily form complexes with perovskite and induce the perovskite dissociation.

李志成, 王亚凌, 杨银, 曹焕奇, 秦文静, 杨利营, 纪伟伟, 印寿根. 利用吡啶添加剂提高钙钛矿太阳能电池的光伏性能[J]. 发光学报, 2017, 38(11): 1503. LI Zhi-cheng, WANG Ya-ling, YANG Yin, CAO Huan-qi, QIN Wen-jing, YANG Li-ying, JI Wei-wei, YIN Shou-gen. Improvement of The Performance of Planar Heterojunction Perovskite Solar Cells by Using Pyridine as Additive[J]. Chinese Journal of Luminescence, 2017, 38(11): 1503.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!