感应加热辅助Si细化激光熔覆沉积TC4晶粒的研究 下载: 1030次

Silicon Refinement of TC4 Grains by Induction Heating Assisted Laser Cladding Deposition
作者单位
1 西安交通大学金属材料强度国家重点实验室, 陕西 西安 710049
2 西安交通大学机械制造系统工程国家重点实验室, 陕西 西安 710049
摘要
在TC4粉末中加入不同含量的Si粉末进行激光熔覆沉积试验,研究了感应加热对试样微观组织的影响。结果表明,在没有引入感应加热的沉积态试样中,Si能够有效地细化柱状晶,柱状晶宽度由285.5 μm减小至12.1 μm。引入感应加热后,试样中柱状晶的宽度未变,但沉积方向上的部分柱状晶被打断,没有形成贯穿生长;晶内组织为α集束,且α片层上析出无规则呈弥散分布的硅化物。
Abstract
The Si powders of different contents are added into the TC4 powders and the laser cladding deposition experiment is conducted. The influence of induction heating on the microstructures of samples is investigated. The results show that, as for the as-deposited samples without the introduction of induction heating, Si can effectively refine the columnar crystals and thus their widths decrease from 285.5 μm to 12.1 μm. In contrast, after the introduction of induction heating, the widths of the columnar crystals do not change, but part of the columnar crystals in the direction of deposition are broken and thus the throughout growth does not form. In addition, the crystals consist of a large number of α colony, and the irregular and dispersed silicide precipitations occur in α lamellar.

李丽君, 王豫跃, 张安峰, 梁朝阳, 李青宇, 张金智, 张晓星. 感应加热辅助Si细化激光熔覆沉积TC4晶粒的研究[J]. 中国激光, 2018, 45(6): 0602006. Lijun Li, Yuyue Wang, Anfeng Zhang, Chaoyang Liang, Qingyu Li, Jinzhi Zhang, Xiaoxing Zhang. Silicon Refinement of TC4 Grains by Induction Heating Assisted Laser Cladding Deposition[J]. Chinese Journal of Lasers, 2018, 45(6): 0602006.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!