发光学报, 2018, 39 (7): 909, 网络出版: 2018-08-30  

溶胶-凝胶法制备Li1.0Nb0.6Ti0.5O3∶Eu3+红色荧光粉

Preparation of Eu3+ Doping Li1.0Nb0.6Ti0.5O3 Red Phosphor by Sol-gel Method
作者单位
1 华南师范大学信息光电子科技学院 广东省微纳光子功能材料与器件重点实验室, 广东 广州 510006
2 湖北大学物理与电子科学学院 铁电压电材料与器件湖北省重点实验室, 湖北 武汉 430062
3 中国科学院 无机功能材料与器件重点实验室, 上海 200050
4 华南师范大学 实验中心, 广东 广州 510006
摘要
采用溶胶-凝胶法制备Li1.0Nb0.6Ti0.5O3∶Eu3+红色荧光粉, 讨论了煅烧温度、煅烧时间以及Eu3+掺杂浓度对样品发光性能的影响。通过XRD、荧光光谱分别对样品的性能进行表征, 结果表明: 样品的晶相结构为“M-相(M-phase)”。在466 nm蓝光激发下, 合成的荧光粉具有橙光(593 nm)和红光(612 nm)发射。发光强度随着煅烧温度的升高先增大后减小, 最佳的煅烧温度为850 ℃。同时, 随着煅烧时间的增加, 发光强度先增大后减小, 最佳煅烧时间为6 h。当Eu2O3掺入质量分数为2.5%时, 样品的发光强度达到最大。Li1.0Nb0.6-Ti0.5O3∶Eu3+红色荧光粉在白光LED的应用中具有潜力。
Abstract
Li1.0Nb0.6Ti0.5O3∶Eu3+ red phosphor was synthesized by sol-gel method. The influences of the sintering temperature, the sintering time and the Eu3+ doping concentration on the luminous properties of the samples were discussed. The properties of the samples were characterized by X-ray diffraction(XRD) and photoluminescence spectroscopy, respectively. The results show that the samples are consist of “M- phase”. Under the excitation of 466 nm, the orange emission at 593 nm and the red emission at 612 nm can be observed. The emission intensity increases with the increasing of the sintering temperature firstly and then decreases. The optimum sintering temperature is about 850 ℃. Moreover, the emission intensity increases with the increasing of the sintering time firstly and then decreases. The relatively high emission intensity of the sample can be obtained when the sintering time is 6 h. In addition, the optimal doping mass fraction of Eu2O3 is about 2.5%. Therefore, the red phosphor has potential application in the white-LED field.

周鹤, 周志勇, 曾群, 姚春凤, 刘磊. 溶胶-凝胶法制备Li1.0Nb0.6Ti0.5O3∶Eu3+红色荧光粉[J]. 发光学报, 2018, 39(7): 909. ZHOU He, ZHOU Zhi-yong, ZENG Qun, YAO Chun-feng, LIU Lei. Preparation of Eu3+ Doping Li1.0Nb0.6Ti0.5O3 Red Phosphor by Sol-gel Method[J]. Chinese Journal of Luminescence, 2018, 39(7): 909.