应用激光, 2018, 38 (4): 597, 网络出版: 2018-10-06  

0.2 mm不锈钢外观件激光精密焊接工艺研究

Study on Laser Precision Welding Process of 0.2 mm Stainless Steel Appearance Parts
作者单位
荆州职业技术学院 湖北 荆州 434020
摘要
采用150 W准连续激光器对0.2 mm 厚的304不锈钢板进行搭接焊接试验, 通过对焊接工艺参数峰值功率、脉冲宽度和离焦量进行正交优化试验, 在保证下层不锈钢外观不被击穿的情况下, 5个焊点的拉力达到28.9 N, 此时最佳的工艺参数为峰值功率300 W, 脉冲宽度6 ms, 离焦量2 mm。将焊点切片数据与正交试验结果结合分析, 结果表明, 对焊点强度影响最大的因素是焊点熔深, 而对熔深影响最大的工艺参数是峰值功率。该实验结果为实际应用中, 激光精密焊接不锈钢薄板外观件提供工艺方法实验指导。
Abstract
A 150 W quasi-continuous laser was used to perform a lap welding test of 304 stainless steel plates with 0.2 mm thick. Through the orthogonal optimization test of welding process parameters of peak power, pulse width, defocusing amount, the tension of 5 welding spots reached to 28.9 N under the condition that the underlying stainless steel was not broken down. The best process parameter at this time were peak power 300 W, pulse width 6 ms, and defocusing amount 2 mm. Combining the welding spots slicing data with the orthogonal test results, the results show that the most important factor for the strength of the welding spots is the penetration, and the process parameter that has the greatest impact on the penetration is peak power. The experiment results provide process method experimental guidance for the practical application of laser welding stainless steel appearance parts.

龚五堂, 雷黎明. 0.2 mm不锈钢外观件激光精密焊接工艺研究[J]. 应用激光, 2018, 38(4): 597. Gong Wutang, Lei Liming. Study on Laser Precision Welding Process of 0.2 mm Stainless Steel Appearance Parts[J]. APPLIED LASER, 2018, 38(4): 597.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!