液晶与显示, 2019, 34 (7): 646, 网络出版: 2019-08-07   

a-Si剩余膜厚对TFT特性的影响

Effect of thickness of a-Si remain on TFT characteristics
作者单位
重庆京东方光电科技有限公司, 重庆400700
摘要
本文通过电学特性测试设备在黑暗(Dark)和光照(Photo)两种测试环境下, 研究了沟道不同a-Si剩余厚度对TFT电学特性的影响。通过调整刻蚀时间改变沟道内a-Si 剩余厚度, 找出电学特性稳定区域以及突变的临界点。实验结果表明: 在黑暗(Dark)环境下a-Si 剩余厚度在30%~48%之间时, TFT器件的电学特性比较稳定, 波动较小; 而剩余厚度少于30%时, TFT特性变差, 工作电流变小, 开启电压变大, 电子迁移率变小; 在光照环境下主要考虑漏电流的影响, 在a-Si剩余厚度43%以内时, 光照 Ioff相对较低(小于Spec 20 pA), 同时变化趋势较缓; 而剩余厚度大于43%时, 光照Ioff增加25%, 同时变化趋势陡峭。综合黑暗和光照测试环境, 在其他条件不变的情况下, a-Si 剩余厚度在30%~43%之间时TFT的电学特性较好, 同时相对稳定。
Abstract
The effects of different a-Si remain thickness of channel on the electrical properties of TFT were studied under dark and photo test environments. The thickness of a-Si remain in channel was changed by adjusting the etching time. Futhermore, the stable region and the critical point of radical change of electrical were found through this experiment. The experimental results show that the electrical characteristics of TFT devices are relatively stable and fluctuate slightly when the thickness of a-Si remain is between 30% and 48% in dark environment. When the remaining thickness is less than 30%, the TFT characteristics become worse, Ion becomes smaller, Vth becomes larger, and the mobility decreases consequently. Unlike dark condition, Ioff is the chief consideration under photo circumstance. When the thickness of a-Si remain is less than 43%, photo Ioff is relatively low (less than spec 20 pA), and the trend of change is relatively slow. But when the residual thickness is more than 43%, photo Ioff increases by 25%, and the trend of change is steep. In conclusion, when the thickness of a-Si remain is between 30% and 43%, the electrical characteristics of TFT are better and relatively stable regardless of test conditions.

田茂坤, 黄中浩, 谌伟, 王恺, 王思江, 王瑞, 董晓楠, 赵永亮, 闵泰烨, 袁剑峰, 孙耒来. a-Si剩余膜厚对TFT特性的影响[J]. 液晶与显示, 2019, 34(7): 646. TIAN Mao-kun, HUANG Zhong-hao, CHEN Wei, WANG Kai, WANG Si-jiang, WANG Rui, DONG Xiao-nan, ZHAO Yong-liang, MIN Tai-ye, YUAN Jian-feng, SUN Lei-lai. Effect of thickness of a-Si remain on TFT characteristics[J]. Chinese Journal of Liquid Crystals and Displays, 2019, 34(7): 646.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!