激光技术, 2020, 44 (3): 299, 网络出版: 2020-06-08  

激光参量对血管支架切缝形貌及粗糙度的影响

Effect of laser parameters on slit morphology and roughness of vascular stents
作者单位
山东理工大学 机械工程学院, 淄博 255049
摘要
为了研究激光加工工艺参量对血管支架切缝形貌以及表面粗糙度的影响, 采用不同参量对比分析试验法, 开展了心血管支架316L材料光纤激光切割实验, 分析了激光脉冲宽度、激光功率和切割速率等不同工艺参量对材料切缝形貌及粗糙度的影响, 得出激光切割支架的最佳工艺参量组合。结果表明, 不同区域切缝形貌和表面粗糙度存在差异性, 其中支架切缝的汽化区厚度主要受脉冲宽度及激光功率影响, 当脉冲宽度为35μs时, 支架切缝汽化区厚度最大可达到120μm; 支架切缝汽化区粗糙度随切割速率增加先减小后增大, 当切割速率为6mm/s时, 切缝表面粗糙度值最低为650nm。此研究结果为心血管支架光纤加工的研究及后续光整加工奠定了理论基础。
Abstract
In order to study the effect of laser processing parameters on the slit morphology and surface roughness of vascular stent, the experiment of optical fiber laser cutting of cardiovascular stent 316L was carried out by means of comparative analysis of different parameters. The effects of different process parameters such as laser pulse width, laser power, and cutting speed on the slit morphology and roughness of the material were analyzed, and the optimum combination of process parameters for laser cutting support was obtained. The results show that there are differences in slit morphology and surface roughness in different regions, in which the thickness of the vaporization zone is mainly affected by the pulse width and laser power. When the pulse width is 35μs, the maximum thickness of the slit vaporization zone can reach 120μm. In addition, the roughness of the slit vaporization zone of the support decreases at first and then increases with the increase of the cutting speed. When the cutting speed is 6mm/s, the lowest value of slit surface roughness is 650nm. The results lay a theoretical foundation for the research and subsequent finishing of cardiovascular stent optical fiber.

赵士伟, 张海云, 李志永, 赵玉刚, 张晋烨. 激光参量对血管支架切缝形貌及粗糙度的影响[J]. 激光技术, 2020, 44(3): 299. ZHAO Shiwei, ZHANG Haiyun, LI Zhiyong, ZHAO Yugang, ZHANG Jinye. Effect of laser parameters on slit morphology and roughness of vascular stents[J]. Laser Technology, 2020, 44(3): 299.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!