发光学报, 2020, 41 (11): 1343, 网络出版: 2020-12-25   

Pr3+掺杂Ge-Ga-Se-CsI硫卤玻璃性能及光纤制备

Pr3+ Doped Ge-Ga-Se-CsI Chalcohalide Glass and Fiber Preparation
作者单位
1 宁波大学信息科学与工程学院 高等技术研究院 红外材料及器件实验室, 浙江 宁波 315211
2 浙江省光电探测材料及器件重点实验室, 浙江 宁波 315211
3 嘉兴学院 南湖学院, 浙江 嘉兴 314001
摘要
采用熔融淬冷法制备了两种浓度的Pr3+掺杂GeSe2-Ga2Se3-CsI(GGC)硫卤玻璃。在2.0 μm激光激励下,比较了玻璃片(2 mm)和玻璃柱(6 mm)的荧光发射光谱。用Judd-Ofelt理论计算分析了Pr3+掺杂Ge-Ga-Se-CsI硫卤玻璃的强度参数Ωi(i=2,4,6)和辐射寿命τrad等光谱参数。通过拟合衰变曲线,测得了玻璃的荧光寿命值(0.5% Pr3+: 3.08 ms)。所制备的光纤具备双包层结构,通过截断法得到光纤在7.6 μm处的最低损耗为2.27 dB/cm。
Abstract
Different series of Pr3+ doped GeSe2-Ga2Se3-CsI(GGC)chalcogenide glass were prepared by a melt-quenching method. Under the excitation of 2.0 μm wavelength, the emission spectra of bulk glass (2 mm) and glass column(6 mm) were compared. The intensity parameter Ωi(i=2, 4, 6) and radiative lifetime τrad of Pr3+ doped Ge-Ga-Se-CsI chalcogenide glass are calculated and analyzed by Judd-Ofelt theory. The fluorescence lifetime of the glass(0.5% Pr3+: 3.08 ms) was measured by fitting the decay curve. The fabricated fiber has a double cladding structure, the fiber loss is measured by cut-back method and the minimum loss at 7.6 μm is 2.27 dB/cm.

汪俊, 冯赞, 吴国林, 汪金晶, 焦凯, 王弦歌, 刘佳, 梁晓林, 徐铁松, 钟明辉, 肖晶, 赵浙明, 刘自军, 刘永兴, 王训四. Pr3+掺杂Ge-Ga-Se-CsI硫卤玻璃性能及光纤制备[J]. 发光学报, 2020, 41(11): 1343. WANG Jun, FENG Zan, WU Guo-lin, WANG Jin-jing, JIAO Kai, WANG Xian-ge, LIU Jia, LIANG Xiao-lin, XU Tie-song, ZHONG Ming-hui, XIAO-Jing, ZHAO Zhe-ming, LIU Zi-jun, LIU Yong-xing, WANG Xun-si. Pr3+ Doped Ge-Ga-Se-CsI Chalcohalide Glass and Fiber Preparation[J]. Chinese Journal of Luminescence, 2020, 41(11): 1343.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!