医用锆基块体非晶合金飞秒激光加工表面特性研究 下载: 1153次

Surface Characteristics of Medical Zr-Based Bulk Metallic Glass Processed by Femtosecond Laser
作者单位
1 安徽建筑大学机械与电气工程学院, 安徽 合肥 230601
2 中国科学技术大学微纳米工程实验室, 安徽 合肥 230022
3 安徽省工程机械智能制造重点实验室, 安徽 合肥 230601
摘要
利用飞秒激光扫描医用锆基块体非晶合金表面制备直线结构,通过扫描电镜观察分析试样表面微观形貌变化,使用接触角测量仪测量加工前后及放置3个月后试样的接触角,并同时使用X射线光电子能谱仪对表面化学成分进行测量分析,最后利用电化学工作站测试其耐腐蚀性。从测试结果可以看出:加工前的锆基块体非晶合金表面表现出一定的亲水性,通过飞秒激光处理后,变为超亲水;在室内用密封袋封装3个月后,飞秒激光加工后的表面的接触角显著增大;测量加工前后样品腐蚀时的开路电压分别为-0.96 V、-0.93 V。经飞秒加工后的非晶合金开路电压更高,与未加工样品相比耐腐蚀性更强。实验结果表明:经飞秒激光表面处理后的非晶合金具有更好的亲水性和耐腐蚀性,增强了作为医用植入体在人体内的适用性。
Abstract
A medical Zr-based bulk metallic glass linear structure was treated by scanning its surface using a femtosecond laser. The surface morphological changes in the samples were observed by scanning electron microscopy. The contact angles of the samples before, directly after fabrication, and three months after fabrication were measured using a contact angle meter, and the surface chemical composition was analyzed by X-ray photoelectron spectrometer. An electrochemical workstation was used to compare the corrosion speed before and after fabrication. Although the initial surface of the Zr-based bulk metallic glass exhibited a certain degree of hydrophilicity, after microstructural surface treatment by a femtosecond laser, the hydrophilicity was considerably improved. The contact angle of the surface after femtosecond laser treatment increased significantly after 3 months of indoor sealing bag preservation. The open-circuit voltage of the samples before and after processing was -0.96 V and -0.93 V, respectively. After the femtosecond processing, the Zr-based bulk metallic glass had a higher open-circuit voltage and better corrosion resistance than the unprocessed sample. Experimental results show that the bulk metallic glass surface treated by the femtosecond laser is more hydrophilic and corrosion resistant, thus enhancing its applicability as a medical implant in the human body.

姚燕生, 葛张森, 陈庆波, 唐建平, 张亦元. 医用锆基块体非晶合金飞秒激光加工表面特性研究[J]. 激光与光电子学进展, 2020, 57(11): 111409. Yansheng Yao, Zhangsen Ge, Qingbo Chen, Jianping Tang, Yiyuan Zhang. Surface Characteristics of Medical Zr-Based Bulk Metallic Glass Processed by Femtosecond Laser[J]. Laser & Optoelectronics Progress, 2020, 57(11): 111409.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!