CdSe量子点敏化对GaAs发光特性的影响 下载: 1143次

Effect of CdSe Quantum Dot Sensitization on GaAs Luminescence Characteristics
作者单位
长春理工大学高功率半导体激光国家重点实验室, 吉林 长春 130022
摘要
为了探究量子点敏化对GaAs衬底发光性能的影响,采用化学沉积法制备了CdSe量子点,将量子点沉积在GaAs衬底上进行敏化。采用X射线衍射测试确认物相,利用扫描电子显微镜对量子点的形貌进行表征,并通过荧光光谱测试对CdSe量子点敏化后的GaAs衬底样品与未敏化的样品进行对比。结果表明:所制备的CdSe量子点大小均匀,尺寸约为20 nm,且均匀地附着在GaAs衬底上,CdSe量子点/GaAs形成了Ⅱ型能带结构。量子点敏化使GaAs衬底表面的载流子浓度升高。通过荧光光谱测试对各发光峰的来源进行了分析。测试数据显示,与敏化前相比,敏化后的GaAs衬底带边发光增强了2.25倍,缺陷发光增强了3倍。
Abstract
In this study, the effect of quantum dot (QD) sensitization on the luminescent properties of GaAs substrates is investigated by preparing CdSe quantum dots via the chemical deposition method and depositing the quantum dots on the GaAs substrates for sensitization. X-ray diffraction is used to confirm the phase, the QD morphology is characterized via scanning electron microscopy, and the sensitized GaAs substrates are compared with the unsensitized ones through fluorescence spectroscopy. Results show that the prepared CdSe quantum dots are uniform in size (approximately 20 nm) and uniformly adhere to the GaAs substrates. CdSe QD/GaAs forms a type-II band structure. Moreover, quantum dot sensitization increases the carrier concentration on the GaAs substrate surface. The source of each luminescence peak is analyzed via fluorescence spectroscopy. Results illustrate that the band-edge luminescence of the sensitized GaAs substrate is 2.25 times higher than that of the unsensitized GaAs substrate. Furthermore, the defect luminescence of the sensitized GaAs substrate is three times higher than that of the unsensitized GaAs substrate.

刘展, 林逢源, 高美, 方铉, 房丹, 王登魁, 唐吉龙, 王晓华, 魏志鹏. CdSe量子点敏化对GaAs发光特性的影响[J]. 中国激光, 2019, 46(8): 0811002. Zhan Liu, Fengyuan Lin, Mei Gao, Xuan Fang, Dan Fang, Dengkui Wang, Jilong Tang, Xiaohua Wang, Zhipeng Wei. Effect of CdSe Quantum Dot Sensitization on GaAs Luminescence Characteristics[J]. Chinese Journal of Lasers, 2019, 46(8): 0811002.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!