中国激光, 2008, 35 (7): 1095, 网络出版: 2008-07-04   

弹性预加载下板料激光喷丸成形特性

Characteristics of Deformation of Plate by Laser Peening under the Elastic Pre-Loading Condition
作者单位
1 安徽工业大学机械工程学院, 安徽 马鞍山 243002
2 江苏大学机械工程学院, 江苏 镇江 212013
摘要
分析了弹性预加载下激光喷丸成形的机制, 并通过试验研究了板料在弹性预加载下激光喷丸成形的特性。试验用的激光脉冲参数为:波长1.06 μm,脉宽23 ns,光斑直径4 mm, 功率密度109 W/cm2量级;试样的材料为LY12CZ硬铝合金。试验结果表明,在弹性预加载下,板料在弹性预弯方向获得的弯矩要比与弹性预弯垂直方向上的弯矩大得多, 弹性预加载下激光喷丸成形可以有效地克服自由状态下激光喷丸件呈球形现象, 激光喷丸件的曲率是自由状态下激光喷丸成形曲率的2~3倍; 在相同曲率下, 弹性预加载下激光喷丸成形件的表面粗糙度比自由状态下激光喷丸成形件的表面粗糙度要低1~2等级, 因此弹性预加载下激光喷丸成形要优于自由状态下的激光喷丸成形。
Abstract
Laser peening forming is a novel technology, which employes the residual stress induced by high-power repetition laser to form plate. The mechanism of laser peening forming under elastic pre-loading condition was analyzed and the feature of deformation was tested by experiments. In the experiments, the parameters of laser were as follows: the wavelength is 1.054 μm, the pulse duration is 23 ns, and the power dsnsity is 109 W/cm2. The material of sample was LY12CZ aeronautic aluminum alloy. The experimetal results show that the flexural moment of the sample in the prebending direction is far bigger than that in the vertical direction to pre-bending and the spherical shape can be conquered during pre-loading laser peening forming to a great extent. Under the same conditions, curvature of workpiece after the pre-loading laser peening is two to three times than that after laser peening without pre-loading, and the surface roughness can be improved by one to two grade. So the laser peening forming during pre-loading is superior to the laser peening without pre-loading.

张兴权, 张永康, 周建忠, 顾永玉, 王正. 弹性预加载下板料激光喷丸成形特性[J]. 中国激光, 2008, 35(7): 1095. Zhang Xingquan, Zhang Yongkang, Zhou Jianzhong, Gu Yongyu, Wang Zheng. Characteristics of Deformation of Plate by Laser Peening under the Elastic Pre-Loading Condition[J]. Chinese Journal of Lasers, 2008, 35(7): 1095.

本文已被 5 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!