532 nm 短/超短脉冲激光作用于蓝宝石的研究

Study on 532 nm Short/Ultrashort Pulse Laser Processing of Sapphire
作者单位
北京工业大学激光工程研究院, 北京 100124
摘要
分别采用波长为532 nm的短脉冲激光(脉宽6 ns)和超短脉冲激光(脉宽15~20 ps)对蓝宝石进行基本作用规律的研究, 探究了多/单脉冲烧蚀点直径与功率的关系, 分析脉冲数与材料阈值的关系, 确定材料阈值。并且对相关作用机理进行系统的对比分析。研究结果表明, 烧蚀点直径的平方与脉冲峰值功率的对数呈线性关系, 根据关系式计算得出光斑半径与实际测量值相符, 并且材料阈值随脉冲数的增加而降低。纳秒绿激光烧蚀蓝宝石材料主要是基于光热作用的机理, 而皮秒激光烧蚀蓝宝石材料在以“电子态”冷去除的同时, 还兼具一些非线性效应。
Abstract
Short pulse (6 ns) laser and vltrashort pluse (15~20 ps) laser with wavelength of 532 nm processing of sapphire were studied. The relation between power and diameter of ablated dot by multi/single-pulse machining was explored to make sure the ablation threshold. In addition, systemic comparison of relative mechanism was discussed. The results showed that the square of ablated dot diameter is proportional to the logarithm of peak pulse laser power. Calculation of the laser spot radius is matched with measured value according to the relation. Besides, the material ablation threshold decreases with the increasing of pulse numbers. The ablation process on sapphire by using 532 nm nanosecond laser is mainly due to the photothermal effect, while the ablation process by picosecond laser was considered to be cold removal based on "electronic state" as well as nonlinear effects.

王亭入, 季凌飞, 燕天阳, 林真源, 王文豪, 李健, 蒋毅坚. 532 nm 短/超短脉冲激光作用于蓝宝石的研究[J]. 应用激光, 2017, 37(2): 251. Wang Tingru, Ji Lingfei, Yan Tianyang, Lin Zhenyuan, Wang Wenhao, Li Jian, Jiang Yijian. Study on 532 nm Short/Ultrashort Pulse Laser Processing of Sapphire[J]. APPLIED LASER, 2017, 37(2): 251.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!