飞秒激光作用下薄膜的阈值损伤到膜层剥落

The evolution of coating threshold damage to peeling off under femtosecond laser irradiation
作者单位
1 国防科学技术大学机电工程与自动化学院, 湖南 长沙 410073
2 中国人民解放军 63880部队光电对抗试验和评估技术重点实验室, 河南 洛阳 471003
3 国防科学技术大学光电科学与工程学院, 湖南 长沙 410073
摘要
在飞秒单脉冲激光损伤 HfO2/SiO2薄膜样品实验中, 随着激光能量密度升高, 膜层从缺陷导致的点损伤发展到整层剥落, 损伤区域轮廓由模糊变清晰.研究表明, 尺度在纳米量级的颗粒缺陷会产生局部的场增强效应, 该效应与薄膜干涉场叠加, 造成了阈值损伤阶段损伤区域出现大量损伤点, 且由于飞秒激光对包括缺陷在内的薄膜材料的本征损伤特性, 使其损伤行为较为确定, 随着激光能量的提升, 薄膜出现更大面积的规则烧蚀区, 此时干涉场的作用上升到主导地位, 膜层的整层剥落行为掩盖了缺陷的诱导作用.
Abstract
In the experiment of HfO2/SiO2 coatings damaged by femtosecond single pulsed laser, the evolution of coating ablation along with increase of the laser energy was observed. The research shows that coating defects even in nanoscale can induce local light field intensification, which superposes on the interference field. As a result, the coating damage in threshold phase is mainly controlled by the particle defects even when irradiated by femtosecond laser. Because of the intrinsic damage characteristic of femtosecond laser to the coating materials including the defects of even distribution, the damage thresholds of these coatings are relatively deterministic. With the increase of pulse energy, the outline of damaged area becomes clearer. In this condition, the contribution of interference field is increasingly dominant compared with the local light field caused by defects, and the phenomena of coating spalling cover up the impact of defects.

石峰, 朱志武, 程湘爱, 戴一帆. 飞秒激光作用下薄膜的阈值损伤到膜层剥落[J]. 红外与毫米波学报, 2017, 36(3): 361. SHI Feng, ZHU Zhi-Wu, CHENG Xiang-Ai, DAI Yi-Fan. The evolution of coating threshold damage to peeling off under femtosecond laser irradiation[J]. Journal of Infrared and Millimeter Waves, 2017, 36(3): 361.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!