基于InPb合金的非制冷焦平面探测器窗口低温焊接工艺研究

Low Temperature Welding of Uncooled Focal Plane Detector Window Based on InPb Alloy
作者单位
1 昆物理研究所, 昆明 6500223
2 昆明市中小企业服务中心, 昆明 650041
摘要
研究了采用纯度为 99.9%的 In70Pb30合金作为焊料片的低温焊接技术, 分析了焊接时候的影响因素: 焊料片的影响、升温速率、焊接温度、真空度, 通过采用甲酸对焊料片预处理去除氧化层, 在 215℃、5×10-7 torr的真空环境下进行了焊接, 焊接后的样品采用 X-ray、拉力测试系统、检漏仪测试了样品的孔洞率、焊接强度、漏率, 结果表明: 焊接后焊接区域合金均匀、无缝隙、孔洞率少、剪切力高、气密性好, 能够满足非制冷焦平面的窗口封接的气密性要求。
Abstract
The low temperature welding technology was studied by the use of the In70Pb30 alloy with 99.9% purity as welding pieces, the influencing factors during welding were analyzed: the influence of welding pieces, heating rate, welding temperature, vacuum degree, the welding pieces were pretreated by the use of formic acid to remove oxide layer, the welding was operated at 215℃, 5×10-7 torr under the condition of vacuum, the samples of after welding were characterized by X-ray, pull test system, leakage detector to test the holes, the welding strength, the leakage rate of the samples, the results indicate that: the good homogeneity of alloy, seamless, less holes, high shear force and good air tightness in welding area after welding, those good properties make the samples satisfy the need of the air tightness of the window sealing of uncooled focal plane.

袁俊, 龚瑜, 冯江敏, 杨璇, 太云见, 何雯瑾, 朱琴, 普朝光, 黎秉哲. 基于InPb合金的非制冷焦平面探测器窗口低温焊接工艺研究[J]. 红外技术, 2017, 39(7): 659. YUAN Jun, GONG Yu, FENG Jiangmin, YANG Xuan, TAI Yunjian, HE Wenjin, ZHU Qin, PU Chaoguang, LI Bingzhe. Low Temperature Welding of Uncooled Focal Plane Detector Window Based on InPb Alloy[J]. Infrared Technology, 2017, 39(7): 659.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!