不同吸光涂层对激光微织构加工性能影响研究

Influence of different light absorbing coating on property of laser surface texturing
作者单位
江苏大学 机械工程学院, 镇江 212013
摘要
为了提高激光微织构加工效率和改善微织构加工质量, 采用W-71s型喷枪在GCr15轴承钢表面分别喷涂用黑漆、水玻璃、黄料、磷酸锌和石墨制备的涂层。利用Nd∶YAG激光加工机对其进行激光微织构加工, 使用3维形貌分析仪对微凹坑的形貌进行了检测。结果表明, 与无涂层试样相比, 采用水玻璃和黄料涂层试样表面蚀除凹坑体积均增加, 凹坑边缘熔渣体积均减少, 其中黄料涂层表面蚀除凹坑体积增加了29.4%, 水玻璃涂层凹坑边缘熔渣体积减少了64.9%; 在一定条件下, 复合涂层相比单一涂层具有更好的激光加工性能, 其中黄料与水玻璃复合涂层的性能最为显著, 与未经涂层的相比, 凹坑蚀除体积增加了47.1%, 凹坑边缘熔渣体积减少了43.2%。这一结果对提高激光微织构加工效率、改善微织构加工质量具有一定的指导意义。
Abstract
In order to improve machining efficiency and the surface quality of laser surface texturing for metal surface, the W-71s type spray gun was used to spray black paint, water glass, yellow material, zinc phosphate and graphite on the surface of GCr15 bearing steels respectively. Then, the samples were processed by Nd∶YAG laser. Finally, the morphology of material was measured by 3-D morphology analyzer. The experimental results show that compared with uncoated specimens, the removing volume and slag volume around the dimple of specimen surface coated with water glass and yellow material increase and decrease respectively. The removing volume of the sample coated with yellow material increases by 29.4% and the slag volume of specimen surface coated with water glass decreases by 64.9%. Compared with single coating, some composite coating has better laser surface texturing performance. The composite coating with water glass and yellow material has great laser surface texturing performance. Compared with uncoated specimens, the removing volume increases by 47.1%, the slag volume decreases by 43.2%. The result is very instructive to improve the machining efficiency and surface quality of laser surface texturing.

华希俊, 丁积霖, 张培耘, 郝静文, 孙建国, 符永宏. 不同吸光涂层对激光微织构加工性能影响研究[J]. 激光技术, 2017, 41(4): 498. HUA Xijun, DING Jilin, ZHANG Peiyun, HAO Jingwen, SUN Jianguo, FU Yonghong. Influence of different light absorbing coating on property of laser surface texturing[J]. Laser Technology, 2017, 41(4): 498.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!