发光学报, 2018, 39 (9): 1233, 网络出版: 2018-09-08   

KY3F10∶Yb3+,Tm3+,Ho3+纳米晶在单一980 nm辐射下的色稳定上转换白光

Color Stable Upconversion White Emission of KY3F10∶Yb3+,Tm3+,Ho3+ Nanocrystals Under Single 980 nm Excitation
作者单位
湖州师范学院 理学院, 浙江 湖州 313000
摘要
利用简单的水热法制备了立方相KY3F10∶15%Yb3+,0.5%Tm3+,0.2%Ho3+上转换纳米晶。在980 nm激发下, 获得接近等能白的上转换发光。上转换机理分析表明, 蓝、绿、红光发射分别源自Yb3+到Tm3+和Ho3+的能量传递。更重要的是, 该上转换白光显示了良好的色稳定性。当泵浦功率由688 mW增加到1 688 mW, 色差仅为0.027 5。其原因在于, 一方面三基色发光的功率关系比较接近; 另一方面蓝光的功率关系随泵浦功率的增加逐渐减小, 而绿、红光的功率关系保持不变。蓝光的饱和现象可能与激光辐射所引起的热效应有关。
Abstract
Cubic KY3F10∶15%Yb3+,0.5%Tm3+,0.2%Ho3+ upconversion nanocrystals were synthesized by a simple hydrothermal method. Under the excitation of 980 nm, the upconversion luminescence with chromaticity coordinates nearby equal energy white was obtained. The analysis of the upconversion mechanism shows that the blue, green, and red emissions originate from the energy transfer from Yb3+ to Tm3+ and Ho3+, respectively. More importantly, it is found that the upconversion white emission shows favorable color stability. When the pump power increases from 688 mW to 1 688 mW, the aberration is only 0.027 5. The reason is that, on the one hand, the power dependences of the three primary colors are relatively close to each other. On the other hand, the power dependence of the blue emission gradually decreases as the pump power increases, while the power dependences of the green and red emissions remain unchanged. The saturation of blue emission may be related to the thermal effect caused by laser radiation.

庞涛, 王玉, 谢建平. KY3F10∶Yb3+,Tm3+,Ho3+纳米晶在单一980 nm辐射下的色稳定上转换白光[J]. 发光学报, 2018, 39(9): 1233. PANG Tao, WANG Yu, XIE Jian-ping. Color Stable Upconversion White Emission of KY3F10∶Yb3+,Tm3+,Ho3+ Nanocrystals Under Single 980 nm Excitation[J]. Chinese Journal of Luminescence, 2018, 39(9): 1233.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!